Nitrogen and fluorine co-doped TiO₂/carbon microspheres for advanced anodes in sodium-ion batteries: High volumetric capacity, superior power density and large areal capacity

Dan Lv,Dongdong Wang,Nana Wang,Hongxia Liu,Shaojie Zhang,Yansong Zhu,Kepeng Song,Jian Yang,Yitai Qian

DOI: https://doi.org/10.1016/j.jechem.2021.11.040

IF: 13.1

2022-01-01

Journal of Energy Chemistry

Abstract:Fast charging and high volumetric capacity are two of the critical demands for sodium-ion batteries (SIBs). Although nanostructured materials achieve outstanding rate performance, they suffer from low tap density and small volumetric capacity. Therefore, how to realize large volumetric capacity and high tap density simultaneously is very challenging. Here, N/F co-doped TiO2/carbon microspheres (NF-TiO2/C) are synthesized to achieve both of them. Theoretical calculations reveal that N and F co-doping increases the contents of oxygen vacancies and narrows the bandgaps of TiO2 and C, improving the electronic conductivity of NF-TiO2/C. Furthermore, NF-TiO2/C exhibits the high binding energy and low diffusion energy barrier of Na+, significantly facilitating Na+ storage and Na+ diffusion. Therefore, NF-TiO2/C offers a high tap density (1.51 g cm(-3)), an outstanding rate performance (similar to 125.9 mAh g(-1) at 100 degrees C), a large volumetric capacity (similar to 190 mAh cm(-3) at 100 degrees C), a high areal capacity (similar to 4.8 mAh cm(-2)) and an ultra-long cycling performance (similar to 80.2% after 10,000 cycles at 10 degrees C) simultaneously. In addition, NF-TiO2/C parallel to Na3V2(PO4)(3) full cells achieve an ultrahigh power density of 25.2 kW kg(-1). These results indicate the great promise of NF-TiO2/C as a high-volumetric-capacity and high-power-density anode material of SIBs. (C) 2021 Science Press and Dalian Institute of Chemical Physics, Chinese Academy of Sciences. Published by ELSEVIER B.V. and Science Press. All rights reserved.