Influence of heat treatment on corrosion behavior of Al–Mn–Mg–Sc–Zr alloy produced by laser powder bed fusion
Zequn Zhang,Jin'e Sun,Junsheng Wu,Jiuyang Xia,Baicheng Zhang,Pengcheng Zuo,Bowei Zhang
DOI: https://doi.org/10.1016/j.jmrt.2023.02.029
IF: 6.267
2023-03-03
Journal of Materials Research and Technology
Abstract:Effect of heat treatments on the microstructure and corrosion behavior of Al–Mn–Mg–Sc–Zr alloy fabricated by laser powder bed fusion (LPBF) were systematically investigated. The results demonstrate that the 300 °C/5 h heat-treatment doesn't alter the typical bimodal grain distribution of LPBF-fabricated alloy. However, the grains at molten pool boundaries experience a significant growth after a 500 °C/5 h heat treatment, narrowing the gap of grain size between fine-grain (FG) region and coarse-grain (CG) region. It is also found that the heat treatments have an impact on Al 3 (Sc, Zr) and Al 6 (Mn, Fe) precipitates. Detailedly, the Al 3 (Sc, Zr) precipitates undergo a slight growth in size and obvious increase in quantity after heat treatment whilst the Al 6 (Mn, Fe) particles go through a rapid increase both in amount and size, especially for the alloy after being subject to a higher temperature heat treatment. As consequence, the heat-treated LPBF aluminum alloys exhibit worse corrosion resistance compared with their original state. The Al 3 (Sc, Zr) precipitates acting as micro-cathodes at molten pool boundaries accelerate the preferential corrosion of fine grain regions of 300 °C/5 h heat-treated alloy (HT-300). In contrast, the 500 °C/5 h heat-treated alloy (HT-500) tends to promote a more uniform corrosion due to the dissolution of the homogeneously distributed Al 6 (Mn, Fe) anodes on the alloy surface.
materials science, multidisciplinary,metallurgy & metallurgical engineering