Abstract:Linear organic-inorganic polyureas (PUreas) with polyhedral oligomeric silsesquioxane (POSS) cages in the main chains were synthesized via polycondensation of diamines with carbon dioxide (CO2). First, 3,13-dianilino double decker silsesquioxane (denoted 3,13-dianilino DDSQ) was synthesized. An alpha, omega-diamino-terminated poly(propylene oxide) as well as the POSS diamine was exploited for polycondensation with CO2; PUrea and PUrea-DDSQ with sufficiently high molecular weights were obtained with various contents of POSS. The morphological investigation shows that the linear PUreas with POSS cages in the main chains were microphase-separated; the POSS cages were aggregated into spherical microdomains with the size of 50-120 nm in diameter. Owing to the introduction of POSS cages, PUrea was transformed from a viscous liquid into elastic solids in the ranges of composition investigated. At room temperature, linear organic-inorganic PUreas behaved as cross-linked elastomers. This behavior is ascribed to the generation of physical cross-linking with POSS microdomains as the cross-linking sites. In addition, the organic-inorganic PUreas displayed self-healing properties via the dynamic exchange of multiple hydrogen bonds. It was found that the self-healing properties were significantly affected by the content of 3,13-dianilino DDSQ.

Organic–Inorganic Polyureas with POSS Cages in the Main Chains Via Polycondensation of Diamines with Carbon Dioxide