Abstract:A series of activated-carbon-supported K-Co-Mo catalysts (K-Co-Mo/AC) were prepared by using a solgel method combined with incipient wetness impregnation. The catalyst structure was characterized by X-ray diffraction (XRD), N-2 adsorption-desorption, X-ray absorption fine structure spectroscopy and X-ray photoelectron spectroscopy, and their catalytic performance toward synthesis of higher alcohols from syngas was investigated. The large surface area and pore volume of the support facilitated the distribution of metal particles and high dispersion of metals. At low Mo loading, the Mo atoms on the activated carbon surface were mainly tetrahedrally coordinated Mo6+ species. With an increase in the Mo loading, the coordination environment of the surface Mo atoms gradually transformed from tetrahedrally coordinated Mo6+ to octahedrally coordinated Mo4+, indicating that an increase in the Mo loading promoted the reduction of Mo6+ species to Mo4+ species. After reduction, it was observed that a type of a lower state Mo delta+ (1 < delta < 4) species was present on the surface, which is suggested to be responsible for alcohol synthesis. Compared to the unsupported catalyst, K-Co-Mo/AC exhibited a significantly higher activity for alcohol formation. In particular, the C2+ alcohol content increased significantly. This can be attributed to the fact that the supported catalysts have a high active surface area, and the mesoporous structure is suggested to prolong the residence time of intermediates to form alcohols in the pores to some extent, thus promoting the formation of higher alcohols. Under the conditions of a Mo/AC weight ratio of 40% and a reduction temperature of 798 K, the K-Co-Mo/AC catalyst exhibited the highest activity for alcohol formation, which may be attributed to the high content of Mo delta+ (1 < delta < 4) species on the surface.

Surfactant-assisted Preparation of Mo-Co-K Sulfide Catalysts for the Synthesis of Low-Carbon Alcohols Via CO2 Hydrogenation

Synthesis of Higher Alcohols from CO 2 Hydrogenation over Mo–Co–K Sulfide-Based Catalysts

Activated Carbon‐Supported Mo‐Co‐K Sulfide Catalysts for Synthesizing Higher Alcohols from CO2

Sol–gel Preparation of K–Co–Mo Catalyst and Its Application in Mixed Alcohol Synthesis from CO Hydrogenation

Mixed Alcohol Synthesis from Syngas on K–Co–Mo/C Catalyst Prepared by a Sol–Gel Method

Mo–Co–K Sulfide-Based Catalysts Promoted by Rare Earth Salts for Selective Synthesis of Ethanol and Mixed Alcohols from Syngas

Effect of KCoMoS2 Catalyst Structures on the Catalytic Performance of Higher Alcohols Synthesis via CO Hydrogenation

COx hydrogenation to methanol and other hydrocarbons under mild conditions with Mo3S4@ZSM-5

Catalytic Properties and Structure of the K-Co-Mo Catalysts Prepared by Sol-Gel Method for Mixed Alcohol Synthesis — Effect of K Content

Bifunctional Catalysts Composed of Low Silicon‐content SAPO‐34 Nanosheets and in 2 O 3 /zro 2 with Improved Performance for CO 2 Hydrogenation

Effect of cobalt promoter on Co–Mo–K/C catalysts used for mixed alcohol synthesis

Influence of Carbonization Conditions on Structural and Surface Properties of K-Doped Mo2C Catalysts for the Synthesis of Methyl Mercaptan from CO/H2/H2S

Edge-rich molybdenum disulfide tailors carbon-chain growth for selective hydrogenation of carbon monoxide to higher alcohols

Effect of Lanthanum Promotion on the Unsupported Mo–Co–K Sulfide Catalysts for Synthesis of Mixed Alcohols from Syngas

Insights into the one-step ethanol synthesis through CO hydrogenation over surfactant-assisted preparation of CuCo/SiO2 catalyst

Alkaline-Etched NiMgAl Trimetallic Oxide-Supported KMoS-Based Catalysts for Boosting Higher Alcohol Selectivity in CO Hydrogenation

Effects of Cobalt Promoter and Reduction Temperature on the Surface Species and Syngas Adsorption of K–Co–Mo/C Catalyst for Mixed Alcohols Synthesis

A highly efficient Li-Cu/MoO x catalyst constructed by a precursor dispersion and alkali metal promotion stepwise regulation strategy for CO 2 hydrogenation to methanol reaction

Ordered mesoporous NiMg bimetal oxides confined KMoS catalyst for selective CO hydrogenation into higher alcohols

Activated-Carbon-Supported K-Co-Mo Catalysts For Synthesis Of Higher Alcohols From Syngas

Sulfur vacancy-rich MoS2 as a catalyst for the hydrogenation of CO2 to methanol