Facile Fabrication of Self-Healing Silicone-Based Poly(urea-Thiourea)/tannic Acid Composite for Anti-Biofouling

Jiawen Sun,Chao Liu,Jizhou Duan,Jie Liu,Xucheng Dong,Yimeng Zhang,Ning Wang,Jing Wang,Baorong Hou

DOI: https://doi.org/10.1016/j.jmst.2022.01.026

2022-01-01

Abstract:A novel silicone-based poly（urea-thiourea）/tannic acid composite（PDMS-P（Ua-TUa）-TA） with excellent mechanical, self-healing and antifouling properties is developed. The multiple dynamic hydrogen bonds formed by thiourea groups, urea groups, and tannic acid（TA） molecules ensured a tough elastomer（ultimate strength: 2.47 MPa） with high stretchability（～1000%）. TA molecules as partial hydrogen bonding cross-linking sites interacted rapidly with urea and thiourea groups before the migration of polymer chains, resulting in fast and efficient self-healing. Scratches on the film completely disappeared within12 min, and the repair efficiency of strength was up to 98.4% within 3 h under ambient condition. Selfhealing behavior was also evaluated in artificial seawater and the healing efficiency（HE） was 95.1%. Furthermore, TA uniformly dispersed in the polymer matrix provides good antibacterial and anti-diatom properties, as well as strong adhesion to the substrate（～2.2 MPa）. Laboratory bioassays against marine bacteria adhesion（～96%, ～95% and ～93% reduction for P. sp., E. coli, and S. aureus, respectively） and diatom attachment（～84% reduction） demonstrated an outstanding antifouling property of the PDMSP（Ua-TUa）-TA. This work provides a promising pathway towards the development of high-performance silicone-based coatings for marine anti-biofouling.