Cationic-Polymer-Functionalized Separator As a High-Efficiency Polysulfide Shuttle Barrier for Long-Life Li–S Battery
Zhenwei Li,Shaoshao Jiao,Di Yu,Qian Zhang,Kang Liu,Jishu Han,Ziyang Guo,Jie Liu,Lei Wang
DOI: https://doi.org/10.1021/acsaem.1c00281
IF: 6.4
2021-03-05
ACS Applied Energy Materials
Abstract:Because of the advantages of high theoretical capacity, low cost, and environmental friendliness, lithium–sulfur (Li–S) batteries have attracted wide attention as promising energy storage system for electric vehicles and smart power grids. However, their commercialization is still greatly restricted by their poor cycle stability, resulting from the severe shuttling of soluble lithium polysulfides (LiPSs) during cycling. Herein, we designed a polymer/rGO (/rGO) blocking layer on a commercial PP separator. Such a blocking layer can strongly fix LiPSs by the electrostatic attraction effect between the cationic polymer backbones and the polysulfide anions. As a result, a Li–S battery equipped with a /rGO-functionalized separator showed much improved cycling stability with a capacity fading rate as low as 0.06% per cycle during 700 cycles at 1 <i>C</i>. Especially, high areal capacity of 6.3 mAh cm<sup>–2</sup> was also achieved with a high sulfur loading of 8.5 mg cm<sup>–2</sup> after 50 cycles. This work highly emphasizes that the electrostatic attraction mechanism between cationic polymers and polysulfides can effectively restrain the polysulfide shuttling and thus significantly improve the electrochemical performance of Li–S batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.1c00281?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.1c00281</a>.SEM image of initial CNTs, TEM image and XPS survey spectrum of , SEM images and XRD patterns of GO and rGO, Raman and N<sub>2</sub> adsorption/desorption isotherm of /rGO, Nyquist plots of /rGO separator and PP separator, CV curves and charge–discharge curves of Li–S batteries with PP separators, long-term cycling performance of the Li–S batteries with /rGO separator at 0.5 and 2 <i>C</i>, CV curves of Li–S batteries with /rGO separator and PP separator for the first cycle at 0.1 mV s<sup>–1</sup>, charge–discharge curves of Li–S batteries with high sulfur loading using /rGO separator and PP separator (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.1c00281/suppl_file/ae1c00281_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels