Abstract:The microstructures and deformation mechanisms of the f.c.c. medium-entropy alloy (MEA) (NiCoCr)76(Ni6AlTi)3 has been analyzed after various thermo-mechanical treatments. The solutionized, single-phase MEA, which had a grain size of 93.4 ± 31.9 μm, was cold-rolled (CR) to a 80% thickness reduction after which it showed both a high yield strength (YS) of 1539 MPa and a high ultimate tensile strength (UTS) of 1602 MPa, but an elongation to failure, ε, of only 16%. The CR MEA was then subjected to one of two heat treatments: (1) the CR MEA was recrystallized at 1100oC for 24 h, which produced a single-phase material with 85 ± 61.7 μm grain size that exhibited a much lower YS and UTS of 364 MPa and 747 MPa, respectively, but a much greater ε of 73%; and (2) the MEA was aged at 700oC for 24 h, which produced a fine-grained (1.1 ± 0.9 μm) material and a high volume fraction (0.35) of 12 nm dia. L12 nanoparticles that exhibited an excellent combination of strength and ductility, viz., YS∼1501 MPa, UTS∼1651 MPa, elongation ∼26%. The grain boundary strengthening and precipitation strengthening were together estimated to account for ∼58% of the YS in the latter material. After deformation, the recrystallized MEA contained numerous stacking faults and a Taylor lattice structure containing domain boundaries and microbands, while the aged MEA exhibited numerous stacking faults and sheared particles. The density of low-angle grain boundaries (LAGBs) in the recrystallized MEA increased by 100 times to 2.2 × 10−1 μm/μm2 while the density of CSL Σ3n boundaries decreased by 71% to 7.8 × 10−3 μm/μm2 after deformation. In contrast, the density of LAGBs in the aged MEA increased by 5 times to 2.6 μm/μm2 while the density of CSL Σ3n boundaries decreased by 57% to 0.6 μm/μm2 after deformation.

Mechanical Properties of a CrCoNi Medium Entropy Alloy in a Gradient Twin Structure

Twin-induced transformation strengthening of CoCrNi-based medium-entropy alloy with a gradient nanostructure

Probing Deformation Mechanisms of Gradient Nanostructured CrCoNi Medium Entropy Alloy

Excellent Strength-Ductility Synergy Properties of Gradient Nano-Grained Structural CrCoNi Medium-Entropy Alloy

Ultrasonic Vibration-Assisted Surface Plastic Deformation of a CrCoNi Medium Entropy Alloy: Microstructure Evolution and Mechanical Response

Achieving a unique combination of strength and ductility in CrCoNi medium-entropy alloy via heterogeneous gradient structure

Enhanced Strength-Ductility Synergy in a Gradient Hetero-Structured CrCoNi Medium-Entropy Alloy

Compressive Mechanical Properties of Gradient Structured CrCoNi Medium-Entropy Alloy under High-Temperature and High-Strain-Rate Coupling

Microstructure and Mechanical Properties of the As-Cast and Annealed CoNiV-based MEAs with Al Addition

Enhancing Strength-Ductility Synergy of CoCrNi-Based Medium-Entropy Alloy Through Coherent L1 2 Nanoprecipitates and Grain Boundary Precipitates

Enhanced strength-ductility synergy of medium-entropy alloys via multiple level gradient structures

Gradient recrystallization to improve strength and ductility of medium-entropy alloy

Phase Reversion Mediated the Dual Heterogeneity of Grain Size and Dislocation Density in an Equiatomic CrCoNi Medium-Entropy Alloy

Strength-ductility Synergy and Grain Refinement Mechanisms in a Co-Cr-Ni Medium-Entropy Alloy with Novel Analogous Harmonic Structure

Strengthening mechanism of CrCoNi medium-entropy alloy from the partially recrystallized structure to the fully recrystallized heterogeneous structure

Additively manufactured high strength and ductility CrCoNi medium entropy alloy with hierarchical microstructure

Gradient nanotwinned CrCoNi medium-entropy alloy with strength-ductility synergy

A quasi-in-situ EBSD study of the thermal stability and grain growth mechanisms of CoCrNi medium entropy alloy with gradient-nanograined structure

Microstructures and deformation mechanisms of the medium-entropy alloy (NiCoCr)76(Ni6AlTi)3

Hierarchical Grain Size and Nanotwin Gradient Microstructure for Improved Mechanical Properties of a Non-Equiatomic CoCrFeMnNi High-Entropy Alloy

Mechanical Properties and Microstructure Evolution of a CrCoNi Medium Entropy Alloy Subjected to Asymmetric Cryorolling and Subsequent Annealing