Abstract:Hollow carbon nanospheres have attracted more and more attention as supercapacitor materials due to their excellent electrical conductivity, high theoretical surface area, high accumulation and rapid ion transfer and diffusion. In this work, we employed the Stöber method to create silica as a template, and then applied self-assembly and dopamine polymerization on the surface of the template to form SiO2@TMB-F127-PDA micelles. Then the nitrogen-doped mesoporous hollow carbon nanospheres (N-MHCNs) were prepared by carbonization and etching on the formed carbon precursors. The effect of dopamine amount on the structure and properties of N-MHCNs was systematically studied. Microstructural characterization results reveal that the morphology of N-MHCNs can be changed from sheet to sphere, and the particle size of N-MHCNs can be 33.8–225.7 nm, the specific surface area is distributed in the range of 175.9–430.1 m2 g−1. Due to the N,O heteroatomic co-doping and Porous spherical structure (with a small particle size of 33 nm, and a large specific surface area of 430.1 m2 g−1), typical sample N-MHCNS-2 shows excellent electrochemical performance in supercapacitors. And it has the highest specific capacitance (241 F g−1) at 0.5 A g−1 current density, excellent rate performance (capacity retention rate of 79 % when current density increases from 0.5 to 10 A g−1) and good cycling ability (capacity retention rate of 90.4 % after 3000 cycles), indicating that it shows great potential in energy storage. This approach provides new opportunities for the controllable synthesis of hollow mesoporous nanospheres and it can be extended to other systems such as hollow metals, metal oxide nanomaterials and carbon-based hybrids.

MnO2 Depositing on the Surface of Hollow Porous Carbon Microspheres for Supercapacitor Application

Synthesis of MnO2/N-doped Ultramicroporous Carbon Nanospheres for High-Performance Supercapacitor Electrodes

Manganese Oxide-Based Electrode Behavior As Materials for Electrochemical Supercapacitors

Manganese Doped Co3O4 Mesoporous Nanoneedle Array for Long Cycle-Stable Supercapacitors

Facile Fabrication of Mesoporous Manganese Oxides As Advanced Electrode Materials for Supercapacitors

Hierarchically Porous MnO2 Microspheres Doped with Homogeneously Distributed Fe3O4 Nanoparticles for Supercapacitors.

Carbon spheres-assisted strategy to prepare mesoporous manganese dioxide for supercapacitor applications

Bamboo fiber-derived porous carbon microspheres decorated with MnO 2 for enhanced supercapacitor performance

Design of MoS2/NC/MnO2 hollow microsphere electrode for high performance supercapacitors

Sodium Dodecylbenzene Sulfonate Assisted Electrodeposition of MnO 2 @C Electrode for High Performance Supercapacitor

Facile Synthesis of Mesoporous MnO2 Microspheres for High Performance AC//MnO2 Aqueous Hybrid Supercapacitors

Preparation of the Cactus-Like Porous Manganese Oxide Assisted with Surfactant Sodium Dodecyl Sulfate for Supercapacitors

Hollow Co3O4@MnO2 Cubic Derived From ZIF-67@Mn-ZIF as Electrode Materials for Supercapacitors

Double-Shelled Mno2 Hollow Spheres for Supercapacitors

Microstructure modification of porous carbon induced by low-dosage manganese nitrate for high-performance supercapacitor electrode

Smart construction of MnCo2O4 microspheres with multiple interiors: Morphological evolution and structure-performance relationship for supercapacitor electrodes

MnHCF/MnO 2 Core-shell Nanostructures As Cathode Material for Supercapacitors with High Energy Density

Cooperative regulation of hard template and emulsion self-assembly to the synthesis of N/O co-doped mesoporous hollow carbon nanospheres for supercapacitors

Interfacial Synthesis of Porous Mno2 and Its Application in Electrochemical Capacitor

The Preparation of Nanostructure MnO_2 for Supercapacitor Electrode Material by Electrodeposition

Preparation Of Carbon cloth/MnO2 Doped with Different Metal Ions for Supercapacitor Electrode