High-Performance Cobalt-Doped Carbon Cloth Supported Porous Fe2o3 Flexible Electrode Material in Quasi-Solid Asymmetric Supercapacitors

Wei Shao,Minglong Li,Xiaodong Wang,Ning Fu,Zhenglong Yang
DOI: https://doi.org/10.1016/j.jallcom.2022.167141
IF: 6.2
2022-01-01
Journal of Alloys and Compounds
Abstract:Iron oxide, as a promising anode material, has environmental friendliness, high theoretical capacitance, and a wide voltage window. Cobalt-doped iron oxide was loaded on flexible carbon cloth (Co-Fe2O3 @CC) via hydrothermal reaction. Cobalt doping changes the iron oxide's crystal structure and improves the con-ductivity of the iron oxide. At the same time, it also increases the oxidation state of iron oxide and improves the pseudocapacitance of the electrode material. The reaction conditions were controlled to prepare iron oxide nano-spheres having porous morphology. The porous structure increases the area where the elec-trode material is reacted. The area-specific capacitance of the Co-Fe2O3 @CC electrode material is 315.6 mF cm-2, which is 137.2% higher than that of pure Fe2O3 @CC(133 mF cm-2). The capacitance is unchanged before and after 200 times of 90 degrees bending. The voltage window of assembled Co-Fe2O3 @CC//Ni-MnO2 @CC asymmetric supercapacitors is 0-2 V. The energy density is 0.96 mWh cm-3 and the power density is 28.6 mW cm-3, which has excellent electrochemical performance. After 4000 cycles at a current density of 10 mA cm-2, the capacitance is maintained at 85%. Flexible asymmetric supercapacitors have potential applications in the field of flexible wearables. (c) 2022 Elsevier B.V. All rights reserved.
What problem does this paper attempt to address?