Temperature Evolution of Composition, Thermal, Electrical and Magnetic Properties of Ti3C2Tx-MXene

Shreyas Srivatsa,Waldemar Tokarz,Janusz Przewoźnik,Tomasz Strączek,Krzysztof Grabowski,Paweł Rutkowski,Tadeusz Uhl,Jan Kulawik,Dariusz Kata,Dominika Madej,Jerzy Lis,Czesław Kapusta
DOI: https://doi.org/10.3390/ma17102199
IF: 3.4
2024-05-09
Materials
Abstract:MXenes are a family of two-dimensional nanomaterials. Titanium carbide MXene (Ti3C2Tx-MXene), reported in 2011, is the first inorganic compound reported among the MXene family. In the present work, we report on the study of the composition and various physical properties of Ti3C2Tx-MXene nanomaterial, as well as their temperature evolution, to consider MXenes for space applications. X-ray diffraction, thermal analysis and mass spectroscopy measurements confirmed the structure and terminating groups of the MXene surface, revealing a predominant single OH layer character. The temperature dependence of the specific heat shows a Debye-like character in the measured range of 2 K–300 K with a linear part below 10 K, characteristic of conduction electrons of metallic materials. The electron density of states (DOS) calculations for Ti3C2OH-MXene reveal a significant DOS value at the Fermi level, with a large slope, confirming its metallic character, which is consistent with the experimental findings. The temperature dependence of electrical resistivity of the MXene samples was tested for a wide temperature range (3 K–350 K) and shows a decrease on lowering temperature with an upturn at low temperatures, where negative magnetoresistance is observed. The magnetoresistance versus field is approximately linear and increases its magnitude with decreasing temperature. The magnetization curves are straight lines with temperature-independent positive slopes, indicating Pauli paramagnetism due to conduction electrons.
materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter
What problem does this paper attempt to address?
Based on the provided text content, the main problem that this paper attempts to solve is to study the composition, thermal, electrical and magnetic properties of titanium carbide MXene (Ti₃C₂Tₓ - MXene) nanomaterials at different temperatures in order to consider its potential uses in space applications. Specifically, the paper focuses on the following aspects: 1. **Composition analysis**: The structure and termination groups on the MXene surface were confirmed by X - ray diffraction (XRD), thermal analysis and mass spectrometry measurements, and it was found that there are mainly single - layer OH characteristics. 2. **Thermal properties**: The specific heat capacity of Ti₃C₂Tₓ - MXene in the range from 2 K to 300 K was studied. The results show Debye characteristics, and there is a linear part below 10 K, which is consistent with the conduction electron characteristics of metallic materials. 3. **Electrical properties**: The change of resistivity of MXene samples with temperature in the range from 3 K to 350 K was tested. It was found that the resistivity decreases as the temperature decreases and shows an upward trend at low temperatures, and the negative magnetoresistance phenomenon was observed. 4. **Magnetic properties**: The change of magnetoresistance with magnetic field was studied. It was found that it is approximately linear and increases as the temperature decreases. The magnetization curve is a straight line with a positive slope and does not change with temperature, indicating the Pauli paramagnetism of conductive electrons. These studies aim to provide basic data for the application of MXene nanomaterials in space technology, especially their performance in extreme environments.