Application of Α-Fe2o3 Nanoparticles in Controlling Antibiotic Resistance Gene Transport and Interception in Porous Media

Yiyang Tian,Xinye Lu,Jie Hou,Jiang Xu,Lizhong Zhu,Daohui Lin

DOI: https://doi.org/10.1016/j.scitotenv.2022.155271

2022-01-01

SSRN Electronic Journal

Abstract:Metal oxide nanoparticles (MONPs) with a large specific surface area are expected to bind with antibiotic resistance genes (ARGs), thereby controlling ARGs' contamination by reducing their concentration and mobilization. Here, adsorption experiments were carried out and it was found that α-Fe2O3 NPs could chemically bind with ARGs (tetM-carrying plasmids) in water with an adsorption rate of 0.04 min-1 and an adsorption capacity of 7.88 g/kg. Mixing α-Fe2O3 NPs into quartz sand column markedly increased the interceptive removal of ARGs from inflow water. The interception rate of 1.0 μg/mL ARGs in ultrapure water (25 mL, 5 pore volumes) through the sand column (plexiglass, length 8 cm, internal diameter 1.4 cm) with 1 g/kg α-Fe2O3 NPs was 1.73 times of that through the pure sand column; the interception rate overall increased with increasing addition of α-Fe2O3 NPs, reaching 68.8% with 20 g/kg α-Fe2O3 NPs. Coexisting Na+ (20 mM), Ca2+ (20 mM), and acidic condition (pH 4.0) could further increase the interception rate of ARGs by 1 g/kg α-Fe2O3 NPs from 21.1% to 86.2%, 90.7%, and 96.2%, respectively. The presence of PO43- and humic acid at environmentally relevant concentrations would not significantly affect the interception of ARGs. In the treatment groups with PO43- and humic acid, the removal rate decreased by only 1.8% and 0.1%, respectively. In addition, the interceptive removal of ARGs by α-Fe2O3 NPs-incorporated sand column was even better in actual surface water samples (87.2%) than that in the ultrapure water (21.1%). The findings provide a promising approach to treat ARGs-polluted water.