Abstract:Ion beam sputtering (IBS) was used to deposit Mo2C catalytic layers on vanadium (V) foils and to prepare Mo2C/ V composite membranes for hydrogen separation and purification. It is found that the sputtering temperature during IBS largely affects the structure and catalytic activity of the as-deposited Mo2C films. A high sputtering temperature facilitates the growth of cubic Mo2C along the catalytically dominant crystal plane, which substantially enhances the hydrogen permeability of Mo2C/V. Typically, the Mo2C/V membranes prepared by IBS at a sputtering temperature of 600 degrees C exhibit a significantly high hydrogen permeability of similar to 6.7 x 10(-8) mol H-2 m(-1) S-1 Pa--0(.5) at a hydrogen permeation temperature of 600 degrees C. This is 2.4 times that of Pd and 2.0 times that of Mo2C/V membranes prepared by conventional magnetron sputtering. The present work demonstrates that IBS is a promising technique to prepare highly permeable and cost-effective Mo2C/V membranes for high temperature hydrogen separation.

Substantial Enhancement of Hydrogen Permeability of Mo2C/V Composite Membranes by Ion Beam Sputtering