Effect of Tantalum Content on Microstructure and Mechanical Properties of Cocrnitax Medium Entropy Alloys

Hao Zhang,Yonggang Tong,XiXi Ji,Hongfeng Huang,Lingwei Yang,Yongle Hu,Xiancheng Zhang,Manyu Hua,Shanhong Cao

DOI: https://doi.org/10.1016/j.msea.2022.143322

IF: 6.044

2022-01-01

Materials Science and Engineering A

Abstract:CoCrNi medium entropy alloy (MEA) has potential applications in cryogenic environment due to its strength and plasticity enhancement at low temperatures. However, the poor strength at the room temperature limits its widespread application. In this work, the alloying element, Tantalum (Ta), was chosen to strengthen CoCrNi MEA and CoCrNiTax MEAs with different Ta content were designed and prepared. The effect of Ta content on the microstructure and mechanical properties of the corresponding alloys were investigated. It was found that Ta-enriched Laves phase was formed due to the addition of Ta element. The alloy's microstructure experienced from hypoeutectic to eutectic, and then to hypereutectic morphology evolution with increasing Ta addition. CoCrNiTa0.4 alloy was a fully eutectic microstructure with fine lamellar colonies. Its yield strength reached about 2150 MPa, which was greatly improved compared with CoCrNi MEA. In order to understand the strengthen mechanism of CoCrNiTax MEAs, strength contribution of the alloy's individual phase to the lamellar colonies was investigated by the high-throughput nanoindentation mapping technique. It is indicated that Laves phase had very high hardness increasing from asymptotic to 16.12 GPa to asymptotic to 18.14 GPa, almost 3 times than that of FCC phase (asymptotic to 6.03 GPa). The strengthening of CoCrNiTax MEAs should be attributed to the production of the hard Laves phase and lamellar colonies.