Ion Irradiation Activated Catalytic Activity of MoSe2 Nanosheet for High‐Efficiency Hydrogen Evolution Reaction
Liqiu Huang,Guo Wei,Jiaqi Wang,Derun Li,Shuangfeng Jia,Shixin Wu,Tao Jiang,Yakun Guo,Yichao Liu,Feng Ren
DOI: https://doi.org/10.1002/aenm.202300651
IF: 27.8
2023-06-12
Advanced Energy Materials
Abstract:The introduction of Mo and Se vacancies both on the surface and inside of MoSe2 nanosheets is acheived using He+ irradiation to activate the inert basal plane. The high‐density active sites significantly reduce the overpotential of MoSe2 and greatly enhance the hydrogen evolution reaction stability at industry‐level large current density. Developing highly efficient, low cost, and stable electrocatalysts that work at a large current density is crucial for upgrading the current industrial electrochemical water splitting to produce H2. Molybdenum selenide (MoSe2) is a promising 2D transition metal dichalcogenide (TMD), however, its reported output is inadequate due to its inert basal plane. Herein, the catalytic activity of MoSe2 nanosheet arrays is activated by a novel and controllable method of He+ ion irradiation to introduce multiple vacancies simultaneously into their inert basal planes. The vacancies activated MoSe2 have improved electrocatalytic performance and stability with a minimum overpotential of 90 mV at 10 mA cm−2, a Tafel slope of 49 mV dec−1 and high stability of 650 h at the industry‐level large current density of 1000 mA cm−2 compared to several hours for the pristine sample. The DFT results reveal that single Se and single Mo vacancies on the MoSe2 basal plane can efficiently increase the electrical conductivity and reduce energy barriers for water dissociation and subsequent proton adsorption, thus improving the electrocatalytic capability. This finding proves the application of ion beam in defect engineering for effective hydrogen evolution in TMDs‐based catalysts.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,energy & fuels