Oxygen-vacancy-rich Fe₃O₄/carbon nanosheets enabling high-attenuation and broadband microwave absorption through the integration of interfacial polarization and charge-separation polarization

Zhe Su,Wanyu Zhang,Jiawei Lu,Liying Tian,Shan Yi,Yayun Zhang,Shenghu Zhou,Bo Niu,Donghui Long

DOI: https://doi.org/10.1039/d2ta00080f

IF: 11.9

2022-01-01

Journal of Materials Chemistry A

Abstract:Metal-oxide/carbon composites with remarkable dielectric-magnetic properties are promising as microwave absorption materials, but achieving high-attenuation and broadband microwave absorption properties still remains challenging. Herein, we develop a one-step carbonization of the ferric gluconate precursor to manufacture two-dimensional oxygen-vacancy-rich Fe3O4/carbon nanosheets (Fe3O4/C) for high-attenuation microwave absorption. The key to the synthesis is employing the Fe3+-gluconate complex as the precursor, which has the ability to release small molecules within the viscosity foaming window to spontaneously obtain a 3D self-foamed material. Followed by high-temperature annealing, the as-obtained Fe3O4/C hybrid composite features large lamellar (>20 mu m) carbon nanosheets with abundant yolk-shell heterostructures and highly dispersed and high-loaded (similar to 44%) oxygen-vacancy-rich Fe3O4 nanocrystals. The unique 2D structure could facilitate multiple scattering absorption and interconnect into a 3D conductivity-loss network. Meanwhile, the abundant yolk-shell heterostructures could trigger extra interfacial polarization. And density functional theory calculation results demonstrate that oxygen vacancies endow magnetic Fe3O4 nanocrystals with charge-separation induced polarizations. Consequently, Fe3O4/C exhibit superior microwave absorption capability with an impressive reflection loss (RL) of -65.4 dB and an ultra-broad effective absorption bandwidth of 6.24 GHz. The spontaneous foaming strategy in this work could provide feasible technological approaches for the practical fabrication of microwave absorption materials.