Electric and Magnetic Properties of Cold Sintered SrFe12O19–NaCl Composites in Ka-band

Jiao Du,Ying Liu,Tingchuan Zhou,Lixian Lian,Renquan Wang

DOI: https://doi.org/10.1016/j.ceramint.2022.01.206

IF: 5.532

2022-01-01

Ceramics International

Abstract:(1-x)SrFe12O19-xNaCl (x = 10, 20, 30, 40 and 50 wt%) composites were successfully prepared by cold sintering at a low sintering temperature of 150 degrees C and a uniaxial pressure of 300 MPa, and their structure and properties were systematically investigated. Dense SrFe12O19-NaCl composites were achieved with relative density up to 98.2%. X-ray diffraction, scanning electron microscopy and energy dispersive spectroscopy showed the coexistence of SrFe12O19 and NaCl phases in all composites with no observation of any impurity phases. As NaCl concentration increased, the real part of permittivity (epsilon'), the real part of permeability (mu'), dielectric losses (tan delta(epsilon)) and magnetic losses (tan delta(mu)) decreased. The composites with x >= 40 wt% exhibited high and stable Electric and magnetic performances in 26.5-30 GHz, including epsilon' of 7.5-8.6, mu' of 1.1-1.2, tan delta(epsilon) of 0.01-0.06 and tan delta(mu) of 0.01-0.05, which were attractive for the applications of millimeter wave enabled components.