Ultrahigh Energy Storage Characteristics of Sodium Niobate-Based Ceramics by Introducing a Local Random Field
Feihong Pang,Xiuli Chen,Congcong Sun,Junpeng Shi,Xu Li,Hongyun Chen,Xiaoyan Dong,Huanfu Zhou
DOI: https://doi.org/10.1021/acssuschemeng.0c05265
2020-09-09
Abstract:Lead-free ceramic capacitors are widely applied for novel pulse power supply systems owing to their environmental friendliness, high power density, and fast charge–discharge characteristics. Nevertheless, the simultaneous achievement of a higher recoverable energy storage density (<i>W</i><sub>rec</sub>) and efficiency (η) is still challenging and must be investigated. To obtain a dielectric capacitor with a high <i>W</i><sub>rec</sub> and η, the energy storage characteristics can be improved by reducing the residual polarization and increasing the breakdown strength. In this work, the doping modification of the NaNbO<sub>3</sub> (NN) ceramics is used to produce a local random field to improve the electrical breakdown strength, obtaining a lead-free dielectric capacitor with high energy storage characteristics. According to this strategy, Bi(Ni<sub>0.67</sub>Ta<sub>0.33</sub>)O<sub>3</sub> is added to NN, and an ultrahigh <i>E</i><sub>b</sub> is obtained so that the ceramics have ideal <i>W</i><sub>rec</sub> and η values. 0.85NN–0.15Bi(Ni<sub>0.67</sub>Ta<sub>0.33</sub>)O<sub>3</sub> has a very high <i>W</i><sub>rec</sub> (5.53 J cm<sup>–3</sup>) and η (82.0%) at 575 kV cm<sup>–1</sup>. Furthermore, the energy storage characteristics of the ceramics exhibit good thermal stability and frequency stability that are superior to those of most of the lead-free dielectric capacitors reported to date. In particular, the 0.85NN–0.15 Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub> (0.85NN–0.15BNT) ceramic also allows an ultrafast discharge time (<i>t</i><sub>0.9</sub> = 27.5 ns), large current density (<i>C</i><sub>D</sub> = 506.42 A cm<sup>–2</sup>), and higher power density (<i>P</i><sub>D</sub> = 35.45 mW cm<sup>–3</sup>). These results indicate that (1 – <i>x</i>)NN–<i>x</i>BNT ceramics are promising for applications in lead-free dielectric ceramic capacitors with a high energy storage density and conversion efficiency.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c05265?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c05265</a>.Synthesis process of (1 – <i>x</i>)NN–<i>x</i>BNT and test procedure for (1 – <i>x</i>)NN–<i>x</i>BNT (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c05265/suppl_file/sc0c05265_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology