Synthesis of Gd1 − x Eu x Al3 ( BO 3 ) 4 ( 0 < x ⩽ 1 ) and Its Photoluminescence Properties under UV and Vacuum Ultraviolet Regions

Yuhua Wang,K. Uheda,Hirotsugu Takizawa,Ushirozawa Mizumoto,Tadashi Endo

DOI: https://doi.org/10.1149/1.1383778

IF: 3.9

2001-01-01

Journal of The Electrochemical Society

Abstract:Single phase europium-activated gadolinium aluminum borate, Gd 1 x Eu x Al 3 (BO 3 ) 4 (0 ≤ x ≤ 1) was obtained by the evaporation of its nitrate solution, and calcination at 900 to 1100°C in air. All the solid solution was identified as the isomorphs of huntite. Eu 3+ activated GdAl 3 (BO 3 ) 4 showed intense red emission with CIE chromaticity coordinates of (0.645, 0.330) under 147 nm excitation. According to the excitation and emission spectra, the red emission of Eu 3+ was decreased under excitation of the vacuum ultraviolet (VUV) region (158-160 nm), and increased under excitation UV region (258-260 nm) with the increase of Eu 3+ concentration. In comparison with the absorption data of borates, the 158 nm excitation peak was assigned to the energy level of BO 3 groups. In excitation spectra, the sharp 274 nm peak, corresponding to the 8 S 72 → 6 I 2/11 transition of Gd 3+ in addition to the f-f transitions of Eu 3+ were observed. Consequently, the emission of Eu was induced by the energy transfer of VUV excitation to the activator Eu 3+ ions via the co-activator Gd 3+ in GdAl 3 (BO 3 ) 4 .