General Synergistic Capture-Bonding Superassembly of Atomically Dispersed Catalysts on Micropore-Vacancy Frameworks
Qirui Liang,Wenqiang Li,Lei Xie,Yanjun He,Beilei Qiu,Hui Zeng,Shan Zhou,Jie Zeng,Tianyi Liu,Miao Yan,Kang Liang,Osamu Terasaki,Lei Jiang,Biao Kong
DOI: https://doi.org/10.1021/acs.nanolett.2c00042
IF: 10.8
2022-03-22
Nano Letters
Abstract:Atomically dispersed catalysts are a new type of material in the field of catalysis science, yet their large-scale synthesis under mild conditions remains challenging. Here, a general synergistic capture–bonding superassembly strategy to obtain atomically dispersed Pt (Ru, Au, Pd, Ir, and Rh)-based catalysts on micropore-vacancy frameworks at a mild temperature of 60 °C is reported. The precise capture via narrow pores and the stable bonding of vacancies not only simplify the synthesis process of atomically dispersed catalysts but also realize their large-scale preparation at mild temperature. The prepared atomically dispersed Pt-based catalyst possesses a promising electrocatalytic activity for hydrogen evolution, showing an activity (at overpotential of 50 mV) about 21.4 and 20.8 times higher than that of commercial Pt/C catalyst in 1.0 M KOH and 0.5 M H2SO4, respectively. Besides, the extremely long operational stability of more than 100 h provides more potential for its practical application.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.nanolett.2c00042.Materials and methods; SEM, TEM, and EDX images; EDS elemental mapping and line scan results; size distribution, HRTEM, TEM, and EDX mapping images of Pt NPs; Raman spectra; N2 adsorption isotherms curves; comparison of the specific surface areas of MVF obtained at different temperatures; pore distribution curves of different samples; XPS spectra; FT-EXAFS curves of samples at k space; XRD patterns, HR-TEM images, and corresponding SAED patterns of atomically dispersed catalysts; photograph and STEM images of Pt/MVF synthesized on a large scale; electrochemical impedance spectroscopy (EIS) curves; HER polarization curves, variation of Pt content in MVF; polarization curve recorded for Pt/MVF before and after 5000 CV cycles; XRD, XPS spectra, and AC HAADF-STEM image of Pt/MVF before and after stability test; amperometric curve (i–t) measurements; CVs with different rates; testing device for Faradaic efficiency of H2 evolution; inductively coupled plasma results; EXAFS fitting parameters; comparison of catalytic performance for Pt/MVF with other relevant HER electrocatalysts (PDF)Video S1: Measurement of Faraday efficiency by drainage gas collection method (MP4)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology