Enhanced Photoluminescence of Ba2GdNbO6: Eu3+/Dy3+ Phosphors by Li+ Doping.

Ching-Ching Yu,Xin Liu,Meihua Yu,Cuikun Lin,Chunxia Li,Hui Wang,Jian Lin

DOI: https://doi.org/10.1002/chin.200821013

2008-01-01

ChemInform

Abstract:Abstract The Ba 2 GdNbO 6 : Eu 3+ /Dy 3+ and Li + -doped Ba 2 GdNbO 6 : Eu 3+ /Dy 3+ phosphors were prepared by solid-state reaction process. X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM) and photoluminescence (PL) as well as lifetimes, was utilized to characterize the resulting phosphors. Under the excitation of ultraviolet light, the Ba 2 GdNbO 6 : Eu 3+ /Dy 3+ and Li + -doped Ba 2 GdNbO 6 : Eu 3+ /Dy 3+ show the characteristic emissions of Eu 3+ ( 5 D 0 – 7 F 1,2,3 transitions dominated by 5 D 0 – 7 F 1 at 593 nm) and Dy 3+ ( 4 F 9/2 – 6 H 15/2 , 13/2 transitions dominated by 4 F 9/2 – 6 H 15/2 at 494 nm), respectively. The incorporation of Li + ions into the Ba 2 GdNbO 6 : Eu 3+ /Dy 3+ phosphors has enhanced the PL intensities depending on the doping concentration of Li + , and the highest emission was obtained in Ba 2 Gd 0.9 NbO 6 : 0.10Eu 3+ , 0.01Li + and Ba 2 Gd 0.95 NbO 6 : 0.05Dy 3+ , 0.07Li + , respectively. An energy level diagram was proposed to explain the luminescence process in the phosphors.