Structural Features and Photocatalytic Performance of TiO 2 -Hnbmoo 6 Composite

Lifang Hu,Jie He,Yuan Liu,Yingjie Zhao,Kai Chen

DOI: https://doi.org/10.3866/pku.whxb201512184

2016-01-01

Abstract:: A novel composite material TiO 2 -HNbMoO 6 was prepared by an intercalation-pillar route. The phase and its microstructure, skeleton feature, spectral-response characteristics, and the interaction between interlayer species and nanosheets were characterized using powder X-ray diffraction (XRD), high resolution transmission electron microscopy (HRTEM), laser Raman spectroscopy (LRS), X-ray photoelectron spectroscopy (XPS), UV-Vis diffuse reflectance spectroscopy (UV-Vis DRS), and H 2 temperature-programmed reduction (H 2 -TPR). The specific surface areas of the samples were measured by N 2 adsorption-desorption isotherms. The synergistic effect between the host and the guest of the composites was evaluated by the degradation of methylene blue (MB) dye under simulated sunlight. The results, such as the increase of the d -spacing, the absence of TiO 2 crystalline phase, and the change of the Nb ― O bond in the main body and the Ti ― O bond in TiO 2 before and after composition, demonstrate that TiO 2 is uniformly dispersed in the interlayer of HNbMoO 6 , indicating the interaction between the host laminates and the guest titanium oxide species. The specific surface area of the composite was four times that of its host material, the narrowing band gap, the better adsorption ability, and the superior photocatalytic activity of TiO 2 -HNbMoO 6 were because of the synergistic effect between the host and the guest.