Fabrication and Property Optimization of Electrostatic Spinning PVDF/PDMS Waterproof and Moisture Permeable Membrane
Zhang Qi,Zhou Gaofeng,Yu Hongqin
DOI: https://doi.org/10.1080/10584587.2024.2328858
2024-12-04
Integrated Ferroelectrics
Abstract:This work aims to manufacture PVDF/PDMS waterproof and moisture-permeable membranes. This objective was achieved using the electrostatic spinning in-situ polymerization method proposed by the authors. Furthermore, it was also studied how different PDMS/PVDF content significantly changed nano-fiber membrane properties such as morphology, structure and mechanical properties to improve the properties and morphology of PVDF/PDMS nano-fiber membrane. Both PVDF/DMAc solution and PDMS/THF solution had to be firstly fabricated under certain conditions. Then related equipment was utilized to characterize and test the morphology and properties of PVDF/PDMS nano-fiber membrane. Based on experiments and analysis, it's also explored how different PVDF/PDMS percent impacted on nano-fiber membrane morphology, structure, mechanical properties and waterproof and moisture permeable properties. Results showed that PVDF/PDMS membrane fabricated by electrostatic spinning in-situ polymerization method could easily manufacture PVDF/PDMS waterproof and moisture permeable membrane and that mixing solution with PVDF/PDMS mass ratio 7:3 obviously improved the morphology of waterproof and moisture permeable membrane and physical properties where PVDF/PDMS mass ratio was 7:3, which voltage was 28 kV, which injection speed was 0.5 cm/h and which receiving distance was 20 cm. Furthermore, the morphology of the textile fibrous network was very uniform such as fiber diameter: 150 nm, water contact angle(WCA): 145.7 degrees, air permeability: 3.9 mm/s, hydrostatic pressure: 132 kPa, water vapor transmission: 5115 g/m 2 ·24 h. It was concluded that the method was analytically derived and effective. PVDF/PDMS waterproof and moisture permeable membrane and its manufacturing method could be applied to textile fields and clothing fields.
engineering, electrical & electronic,physics, condensed matter, applied