Abstract:Zinc oxide dust contains various valuable metals of high recovery value; however, the recovery rate of germanium (Ge) from zinc oxide dust remains low in industrial production. To address this challenge, this study investigated the leaching behaviour and occurrence state in the residue of Ge. Mineralogical analysis of Ge-containing zinc oxide dust, combined with sulphuric acid leaching tests, revealed negative correlation between iron (Fe) and silicon (Si) content in the dust and the leaching rate of Ge. Given this finding, the leaching behaviour of Ge and its occurrence state in the leach residue, was further studied using mixed zinc oxide dust (Mixed Dust). This study demonstrated challenges in completely decomposing Ge-containing insoluble phases in the sulphuric acid system, and Ge primarily existed in silicate and insoluble solids (mainly zinc ferrite) with the leach residue, accounting for 69.74% and 18.42% of its distribution, respectively. The insoluble phases of Fe and Si in the leach residue were decomposed through a three-stage enhanced leaching process. The results indicated that the leaching rate of Ge was significantly increased to 95.98% by dissolving insoluble solids such as zinc ferrite and disrupting the lattice of silicate minerals. La poussière d'oxyde de zinc contient divers métaux de valeur ayant une valeur de récupération élevée. Cependant, le taux de récupération du germanium à partir de la poussière d'oxyde de zinc reste faible dans la production industrielle. Pour relever ce défi, cette étude a examiné les raisons du faible taux de lixiviation du germanium (Ge), en se concentrant sur son comportement de lixiviation et son état d'occurrence dans le résidu. L'analyse minéralogique de la poussière d'oxyde de zinc contenant du Ge, combinée à des essais de lixiviation à l'acide sulfurique, a révélé une corrélation négative entre la teneur en fer (Fe) et en silicium (Si) de la poussière et le taux de lixiviation du Ge. Étant donné ces résultats, on a étudié davantage le comportement de lixiviation de Fe, Si et Ge dans un système d'acide sulfurique, ainsi que l'état d'occurrence du Ge dans le résidu de lixiviation, en utilisant de la poussière d'oxyde de zinc mélangée (Poussière Mixte). L'étude a démontré les défis liés à la décomposition complète des phases insolubles contenant du Ge dans le système d'acide sulfurique. L'adsorption de Ge sur le Si a conduit à la précipitation de Ge dans le résidu. Par conséquent, le Ge existait premièrement dans les silicates et les solides insolubles (principalement la ferrite de zinc) dans le résidu de lixiviation, tenant compte de 69.74% et 18.42% de sa distribution, respectivement. Les phases insolubles de Fe et Si dans le résidu de lixiviation ont été décomposées par un procédé de lixiviation améliorée en trois étapes. Les résultats ont indiqué que le taux de lixiviation du Ge avait considérablement augmenté jusqu'à 95.98% en dissolvant des solides insolubles tels que la ferrite de zinc et en perturbant le réseau des minéraux silicatés.

Research on the Behavior of Germanium in the Leaching Process of Germanium-Bearing Zinc Oxide by Sulfuric Acid

Study on leaching behaviour of germanium and iron in zinc oxide dust from lead zinc smelting

Major Obstacles Hindering Gallium and Germanium Leaching in the Zinc Refining Process

Research on the mechanism of lead sulfate adsorption of germanium and ultrasonic inhibition during the leaching process of zinc oxide dust containing germanium

Comparison of ultrasonic-assisted and regular leaching of germanium from by-product of zinc metallurgy

Mechanism and Kinetic Study on Ultrasonically Enhanced Reduction Leaching of Zinc Suboxide

Studies on Recovery of Valuable Metals by Leaching Lead–Zinc Smelting Waste with Sulfuric Acid

Efficient extracting germanium and gallium from zinc residue by sulfuric and tartaric complex acid

Mechanism of Germanium Adsorption by Iron Hydroxide Colloids during the Leaching Process of Secondary Zinc Oxide

Migration behavior of germanium and its related elements in zinc hydrometallurgy process

Inhibition of Fe4Ge3O12 formation in the leaching process of zinc oxide dust containing germanium by ultrasonic and iron powder

Ultrasonic-enhanced sulfuric acid leaching kinetics of high-grade germanium-containing materials

Recent advances in the recovery of germanium during the zinc refining process

Leaching of liquation-feeding furnace dross as a first step for germanium recovery

The States and Properties of Germanium in Sulfuric Acid Solution

Dissociation of germanium-containing insoluble mineral phases in zinc oxide dust Dissociation des phases minérales insolubles contenant du germanium dans la poussière d'oxyde de zinc

Selective Leaching of Germanium and Indium from Dezincification Oxidized Hard Zinc Slag with Oxygen Pressure Leaching Process

Strong magnetic and ultrasonic fields enhanced the leaching of Ga and Ge from zinc powder replacement residue

Study on ultrasonic depolymerization of Si-Ge precipitation in zinc oxide dust leaching process

Hydrochloric Acid Leaching Kinetics Study of Germanium Concentrate

Study on the mechanism of ultrasonic enhanced removal of zinc and germanium from lead residue