Abstract:The residual crack defects on the surface of potassium dihydrogen phosphate (KDP) crystals are the bottleneck that limits the improvement of laser damage resistance in the application of high-power laser devices. The multiple stress waves introduced by these residual surface lateral cracks on crystals under laser irradiation are the main inducement for damage extension and reduction of laser damage resistance. However, the coupling of these stress waves complicates their propagation in the crystal, and the interaction mechanism between each stress wave and laser damage has not been quantitatively characterized. Herein, a laser damage dynamic model for surface lateral cracks is constructed to reproduce the dynamic behaviors of the evolution of micro-defects to sub-millimeter damage pits under laser irradiation. Combined with the time-resolved pump and probe technique, the distribution of stress waves induced by lateral cracks was detected in situ to determine the type of stress waves. Then, the initiation and extension of laser damage were analyzed quantitatively to establish the correlations between different stress waves and damage extension. It is found that the longitudinal, shear, and Rayleigh waves induced by lateral cracks lead to large crush zones on the surface of KDP crystals, as well as butterfly-like damage sites accompanied by a large number of cracks at the bottom in the longitudinal section. The scale of the damage site can reach up to approximately 150 µm for lateral crack defects with large surface widths. This study ultimately reveals the physical mechanism of damage evolution induced by lateral cracks, providing effective guidance for developing control standards of surface crack defects during optical ultra-precision machining processes. This is of great significance for the improvement of laser damage resistance of KDP crystals in high-power laser systems.

Evolution of Laser-Induced Bulk Damage in KDP Crystal

High‐laser‐damage‐threshold potassium dihydrogen phosphate crystals

Initial Damage and Damage Growth of KDP Crystals Induced by 355 Nm Pulse Laser

Recent Advances in Laser-Induced Surface Damage of KH2PO4 Crystal

Determination of Stress Waves and Their Effect on the Damage Extension Induced by Surface Defects of KDP Crystals under Intense Laser Irradiation

Study of Morphological Feature and Mechanism of Potassium Dihydrogen Phosphate Surface Damage under a 351 Nm Nanosecond Laser.

Transient Dynamic Behavior During Nanosecond Laser-Induced Damage Initiated by Surface Defects on KDP Crystals with Simulation and Experimental Method

Characteristics of 355 Nm Laser Damage in KDP and DKDP Crystals

Surface damage evolution of KDP crystals induced by conical cracks under irradiation of nanosecond laser

Investigation and Analysis of Pin-Point Damage and Damage Growth Characteristics in KDP and DKDP Crystals.

Initial energy deposition and initiation mechanism of nanosecond laser damage caused by KDP surface micro-defects

Laser damage evolution by defects on diamond fly-cutting KDP surfaces

Laser Induced Damage Of Potassium Dihydrogen Phosphate (Kdp) Optical Crystal Machined By Water Dissolution Ultra-Precision Polishing Method

Growth Characteristics and Mechanism of Surface and Bulk Damage in KDP and DKDP Crystals

Model Development for Nanosecond Laser-Induced Damage Caused by Manufacturing-Induced Defects on Potassium Dihydrogen Phosphate Crystals

Dynamic behavior modeling of laser-induced damage initiated by surface defects on KDP crystals under nanosecond laser irradiation

On the Ultra-Precision Fabrication of Damage-Free Optical KDP Components: Mechanisms and Problems

Time-resolved Studies of Laser Damage Processes in DKDP Crystals

Determination of Intrinsic Defects of Functional KDP Crystals with Flawed Surfaces and Their Effect on the Optical Properties

Research on Laser-induced Damage Mechanisms of KDP Crystals

Ultraviolet Laser-Induced Damage Characteristics of 70% Deuterated Potassium Dihydrogen Phosphate Crystals