Abstract:Today’s anode for lithium ion batteries is dominated by graphite, with a low operate voltage at 0.1 V vs. Li+/Li, easy to format lithium dendrite and cause to safety risk. As an alternative anode material, the “zero-strain” spinel structure Li4Ti5O12 could avoid Li plating with a relative high intercalation potential (1.55 V vs. Li+/Li) and exhibits an excellent cycling stability. However, the slightly low capacity and high voltage of Li4Ti5O12 result in low energy density. Herein, we report several polyanion-type anode materials for Li (Na)-ion Batteries (Figure 1). Figure 2 gives the crystal structure of Li2TiSiO5, which is illustrated as a layered structure with infinite sheets of distorted TiO6 octahedra and SiO4 tetrahedra, linked by Li atoms. The distorted TiO6 octahedral and SiO4 tetrahedral networks are thought to be the origin of the structural stability of this material. Figure 2 gives the typical charge/discharge curve of Li2TiSiO5 at between 0 and 3 V (vs. Li+/Li), delivers a reversible charge capacity (Li-ion extraction) of 308 mAh/g, with a voltage plateau below 1.0 V. Fig. 1 (a) Phase diagram of polyanion-type materials. (b) Crystal structure of Li2TiSiO5 and (c) typical charge/discharge curve References： [1] Y-Y Xia, et al. Energy Environ. Sci. 2017, 10 , 1456-1464; [2] Y-Y Xia, et al. Electrochim. Acta, 2018, 260, 695-702; [3] Y-Y Xia, et al. ACS Appl. Energy Mater. 2018, doi10.1021/acsaem.8b01412. Figure 1

Polyanion-Type Anode Material for Lithium-Ion Batteries