Metal–Organic Framework Derived Ultrafine Sb@Porous Carbon Octahedron via In Situ Substitution for High-Performance Sodium-Ion Batteries
Qinghua Li,Wang Zhang,Jian Peng,Wei Zhang,Zhixin Liang,Jiawei Wu,Jiajun Feng,Haixia Li,Shaoming Huang
DOI: https://doi.org/10.1021/acsnano.1c05458
IF: 17.1
2021-08-20
ACS Nano
Abstract:Alloying-type anode materials are regarded as promising alternatives beyond intercalation-type carbonaceous materials for sodium storage owing to the high specific capacities. The rapid capacity decay arising from the huge volume change during Na+-ion insertion/extraction, however, impedes the practical application. Herein, we report an ultrafine antimony embedded in a porous carbon nanocomposite () synthesized via facile in situ substitution of the Cu nanoparticles in a metal–organic framework (MOF)-derived octahedron carbon framework for sodium storage. The composite displays an appropriate redox potential (0.5–0.8 V vs Na/Na+) and excellent specific capacities of 634.6, 474.5, and 451.9 mAh g–1 at 0.1, 0.2, and 0.5 A g–1 after 200, 500, and 250 cycles, respectively. Such superior sodium storage performance is primarily ascribed to the MOF-derived three-dimensional porous carbon framework and ultrafine Sb nanoparticles, which not only provides a penetrating network for rapid transfer of charge carriers but also alleviates the agglomeration and volume expansion of Sb during cycling. Ex situ X-ray diffraction and in situ Raman analysis clearly reveal a five-stage reaction mechanism during sodiation and desodiation and demonstrate the excellent reversibility of for sodium storage. Furthermore, post-mortem analysis reveals that the robust structural integrity of can withstand continuous Na+-ion insertion/extraction. This work may provide insight into the effective design of high-capacity alloying-type anode materials for advanced secondary batteries.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsnano.1c05458.SEM images of Cu(btc)3 MOF, , , and commercial microsized Sb; TEM image of ; XRD pattern of commercial microsized Sb and the residue after TGA analysis; Raman spectrum of ; BET curves of Cu(btc)3 MOF and ; XPS survey spectrum of ; electrochemical performance (the first five charge–discharge profiles, cycling performance, EIS curves, the fitted Rct values, and kinetics analysis of the electrochemical behavior) of and other samples; SEM and TEM images of the electrode after cycling (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology