Fabrication of Graphene-PtPd Alloys with High Electro-Catalytic Activity for Ethanol Oxidation

Xiaomei Chen,Munetaka Oyama,Xi Chen
DOI: https://doi.org/10.1149/ma2013-02/3/153
2013-01-01
ECS Meeting Abstracts
Abstract:Recently, direct ethanol fuel cell (DEFC) has drawn increasing attention as a promising kind of power source due to the lower toxicity, lower membrane permeability and higher energy density of ethanol. However, a significant challenge in the development of DEFC technology is the need for highly active catalysts for the ethanol oxidation reaction (EOR) in an acid or alkaline environment that involve complete oxidation per ethanol molecule to CO2, which is difficult to implement at low temperatures. Pt-based alloy (Pt-M) catalysts, which enhance electro-catalytic activity due to their increase of Pt d-band vacancy and more favorable Pt-Pt inter-atomic distance, are well studied and widely used in DEFC [1]. In addition, in order to further maximize the activity of Pt-M catalysts and minimize the use of previous metals, it is helpful to load Pt-M catalysts on the surface of supporting nano-materials with low cost, high surface area, and good electrical conductivity. As a newly developed two-dimensional (2-D) carbon support, graphene has received considerable interest due to its outstanding physical and chemical properties [2, 3]. There are more and more examples of Pt-M alloys/graphene hybrids demonstrated to date [4]. However, in order to avoid aggregation of nanoparticles (NPs), many recent methods rely on specific capping agent for surface stabilization. Unfortunately, the presence of these agents around the NPs leads to decreasing their activity sites, which severely affect their chemical activities. Therefore, it is meaningful to develop surfactant-free method to synthesize Pt-M alloys/graphene hybrids. Here, we described a green, one-pot and surfactant-free route to fabricate PtPd alloy NPs on graphene (PtPd ANPs/G) sheet. As a low-cost and green solvent, ethanol was used as the reductant in this preparation. In addition, graphene sheets were used as a supporting material and stabilizing agent for the deposition of PtPd ANPs. The morphology, structure and composition of the resulting PtPd ANPs/G sheets were characterized by transmission electron microscopy (TEM), high resolution TEM and high-angle annular dark-field scanning TEM (HAADFSTEM). Fig. 1A-C shows the representative TEM images of PtPd ANPs/G at different magnifications. Lowmagnification TEM images (Fig. 1A and B) show that all the PtPd ANPs are uniformly distributed on the graphene surface. The absence of isolated PtPd ANPs in the product indicates a strong interaction between graphene and PtPd ANPs. The HRTEM image in Fig. 1C demonstrates the average diameter of the PtPd ANPs is about 7.6 nm. The inter-planar spacing is 0.192 nm, which agrees well with the (200) lattice spacing of face-centered-cubic (fcc) Pt and Pd. The elemental distribution of the PtPd ANPs/G catalyst was studied by HAADF-STEM technique. The results revealed that both Pt and Pd have a homogeneous distribution on the nanoparticles, suggesting the formation of an alloy structure. Fig. 1 (A-C) Representative TEM (A, B) and HRTEM (C) images of PtPd ANPs/G hybrids.
What problem does this paper attempt to address?