Pt and Its Alloy Nanofibers Made by Electrospinning and Their Application in PEM Fuel Cell

Jianglan Shui,James Li
DOI: https://doi.org/10.1149/ma2009-01/9/461
2009-01-01
ECS Meeting Abstracts
Abstract:Pt catalyst is the crucial component in Proton Exchange Membrane Fuel Cells (PEMFC). Short life and high cost of Pt are the main obstacles for the commercialization of proton exchange membrane fuel cells. In the conventional design, the agglomeration of Pt nanoparticles cannot be avoided; this is the main reason for electrochemical degradation. Furthermore, these nanoparticles cannot stand alone. They are usually supported by carbon nanoparticles, which are prone to oxidation and corrosion over time as well as detachment from the Pt particles. This research aims at finding a new form of Pt-based catalyst. Pt nanowires were chosen because of their structure stability without the need of a support. The electrospinning method was used to make Pt and Pt alloy nanowires, which form a self-supporting net, avoiding the agglomeration problem of nanoparticles. This research began with producing Pt nanowires and studying the influences of various parameters on the composite fiber morphology. The major problems of avoiding the formation of beads along the nanowires and reducing the wire diameters to several nanometers were investigated. To our knowledge, 5~6 nm thick Pt nanowires are the thinnest that have been produced by electrospinning at present. They are still larger than the diameters of Pt nanoparticles in the commercial catalyst (~3 nm). In further research, a method was found to make long, continuous, and yet porous PtFe alloy nanowires with large surface area per unit mass. These wires can stand alone, without support. The overall wire diameter is about 10~20 nm and since it is porous, the ligament size is only about 2 to 3 nm. Electrochemical tests indicated a surface area as high as 55 m2/g Pt. The large films (~1 μm thickness) composed of porous PtNiFe alloy nanowires were used in a membrane electrode assembly (MEA) as the cathode catalyst layer. This MEA offered large active surface area (>60 m2/mg Pt), high current level (>5 A/mg Pt), high power density (~2 W/mg Pt) and very good durability compared with commercial Pt/C nanoparticle catalysts. To save more Pt, a new platinum alloy catalyst was designed—a PtNi nanowire covered with a platinum shell. The core-shell long nanowires had diameters approximately 10~20 nm. They were made by electrospinning followed by acid and heat treatment. The resultant Pt-shell nanowires can prevent nickel (>70 atom%) from dissolving in 1M hot sulfuric acid. At this point, very thin, very porous and even core-shell structure Pt alloy nanowires have been made using the electrospinning technique. Unfortunately, in electrochemical tests it was found that Pt alloy nanowires are not as stable as expected for use as cathode catalysts in fuel cells. Despite its 1-D structure, the leaching of non-noble metals and the diffusion of Pt could not be avoided when Pt diameters were very small (3~4 nm). Therefore, it is believed that thick carbon nanofibers covered with a thin Pt shell may be the path to pursue the production of a stable and economical catalyst.
What problem does this paper attempt to address?