Hydrothermal Preparation and Characterization of Zn, Si, Mg, Fe Doped Hydroxyapatite
S. Keke,Huang Hao,An-chun Yang,Duan Ke,Meng-jie Lu,Weng Jie
DOI: https://doi.org/10.15541/JIM20200664
IF: 1.292
2021-01-25
Journal of Inorganic Materials
Abstract:: Doping of trace elements is an effective way to endow hydroxyapatite with more biological functions. But how about different element doping remained to be further revealed. Here, nine kinds of hydroxyapatite particles containing zinc, silicon, magnesium, iron, manganese, copper, strontium, selenium, and cobalt, respectively, were prepared by parallel hydrothermal synthesis, and their physicochemical properties were studied. The results show that the morphology and crystal growth direction of hydroxyapatite particles are significantly changed, while the phase composition is maintained. The peak intensity of (211) and (112) plane diffraction peaks decreased, accompanied by decreased crystallinity. Analysis results show that the actual doping efficiency obeys the tendency of manganese > zinc > magnesium > iron (trivalent) > strontium > cobalt > copper > selenium > silicon. Among these elements, doping amount of Mn, Zn and Mg is higher, due to their ion radiuses are closed to that of Ca 2+ . The low doping efficiency of copper is caused by its complexation with ammonia in synthetic solution, while silicon and selenium are caused by different geometry and charge of SiO 32- , SeO 32- from that of PO 43- ). This study reveals the reasonable relationship between doping behavior and ion characteristics, providing a useful reference for the design and development of functionalized hydroxyapatite.
Materials Science