High and durable performance of an external-manifold designed reversible solid oxide cell stack
Jiajun Yang,Jiahui Li,Bo Liu,Dong Yan,Lichao Jia,Xiaotao Han,Kaiming Wu,Jian Li
DOI: https://doi.org/10.1016/j.jpowsour.2023.233390
IF: 9.2
2023-07-08
Journal of Power Sources
Abstract:A 5-cell reversible solid oxide cell stack in external-manifold design is fabricated with planar cells with an active area of 169 cm 2 , Ni–Y 2 O 3 stabilized ZrO 2 (Ni-YSZ) support, Ni-YSZ functional anode (fuel electrode), YSZ electrolyte, and YSZ-composite cathode (air electrode). It is operated at various temperatures in different atmospheres. In fuel cell mode at 750 °C with H 2 fuel and air oxidant, the stack generates 407 W (481.7 mW cm −2 , 81.4 W per cell) at 0.68 A cm −2 . In electrolysis mode, with H 2 -55% H 2 O at 750 °C, the current density at the thermo-neutral voltage (6.45 V) is −0.340 A cm −2 , and concentration polarization starts at around −0.3 A cm −2 . They are −0.592 A cm −2 and above −0.50 A cm −2 , respectively, under 80% H 2 O and 800 °C. H 2 production rate increases from 88 NL h −1 to 209 NL h −1 , accordingly. Using H 2 -80% H 2 O for fuel electrode at 800 °C, the stack performs at around 7.0 V and −0.5 A cm −2 for up to 900 h without gas leaking and cell delamination and with more severe metal oxidation at the spots where the SUS430 interconnect contacts with Ni foam current collector on the fuel electrode side.
energy & fuels,materials science, multidisciplinary,electrochemistry,chemistry, physical