Mn4+ nonequivalent-doped Al3+-based cryolite high-performance warm WLED red phosphors

Feng Hong,Haiping Xu,Liu Yang,Guixia Liu,Chao Song,Xiangting Dong,Wensheng Yu

DOI: https://doi.org/10.1039/c9nj03607e

IF: 3.3

2019-01-01

New Journal of Chemistry

Abstract:Mn4+ nonequivalent-doped Al3+-based cryolite red phosphors with controlled morphology and optimized luminescence properties for high-performance warm WLEDs.

What problem does this paper attempt to address?

Synthesis and luminous characteristics of Ba2MgSi2-xAlxO7: 0.1Eu2+, 0.1Mn2+ phosphor for WLED

Changyu Shen,Yi Yang,Shangzhong Jin,Huajun Feng

DOI: https://doi.org/10.1016/j.ijleo.2008.05.009

IF: 3.1

2010-01-01

Optik

Abstract:The shift of the emission band to longer wavelength (yellow-orange) of the Ba2MgSi2−xAlxO7: 0.1Eu2+ phosphor under the 350–450nm excitation range has been achieved by adding the codoping element (Mn2+) in the host. The single-host silicate phosphor for WLED, Ba2MgSi2−xAlxO7: 0.1Eu2+, 0.1Mn2+ was prepared by high-temperature solid-state reaction. It was found experimentally that, its three-color emission peaks are situated at 623, 501 and 438nm, respectively, under excitation of 350–450nm irradiation. The emission peaks at 438 and 501nm originate from the transition 5d to 4f of Eu2+ ions that occupy the two Ba2+ sites in the crystal of Ba2MgSi2−x AlxO7, while the 623nm emission is attributed to the energy transfer from Eu2+ ions to Mn2+ ions. The white light can be obtained by mixing the three emission colors of blue (438nm), green (501nm) and red (623nm) in the single host. When the concentrations of the Al3+, Eu2+ and Mn2+ ions were 0.4, 0.1 and 0.1mol, respectively, the sample presented intense white emission. The addition of Al ion to the host leads to a substantial change of intensity ratio between blue and green emissions. White light could be obtained by combining this phosphor with 405nm light-emitting diodes. The near-ultraviolet GaN-based Ba2MgSi1.7 Al0.3O7: 0.1Eu2+, 0.1Mn2+ LED achieves good color rendering of over 85.
Monodisperse CaAl12O19:Mn4+ Microspheres for Full-Spectrum White LEDs

Zhang Wei,He Mengting,Jia Jiannan,Liu Cong,Xu Qiang,Qiao Xvsheng,Fan Xianping

DOI: https://doi.org/10.1007/s10971-022-05954-2

2022-01-01

Journal of Sol-Gel Science and Technology

Abstract:Non-rare-earth Mn4+-activated red-emitting oxide phosphors have emerged as potential alternatives of typical Eu2+ doped nitrides owing to broad-band absorption, narrow-band emission, high color purity and low cost. In this work, highly efficient CaAl12O19:Mn4+ microspheres with uniform size distributions were first prepared by combining an epoxide-driven sol-gel method with heat treatment in oxygen atmosphere. The spherical morphology is beneficial to reduce scattering of light to enhance the photoluminescence of the phosphor. This phosphor shows red emission attributed to Mn4+: 2Eg → 4A2g spin-forbidden transition in the range of 600~750 nm under excitation at 340 nm. Partitioning Mg2+ in the host was found to enhance Mn4+ luminescence because of charge balance effect and the proposed mechanisms were discussed. The luminescence quantum yield of CaAl11.7576O19:0.0024Mn4+, 0.24Mg2+ microspheres which were heat treated for 4 h at 1300 °C was measured to be 56.1%. The white LED device based on the glass ceramic containing phosphors was found to show a high-color-rendering index of 96 and a low correlated color temperature of 4522 K. The results indicate that CaAl12O19:Mn4+ microspheres have great potential for near-ultraviolet LEDs on full-spectrum lighting.
Flux-assisted low-temperature synthesis of Mn4+-doped unusual broadband deep-red phosphors toward warm w-LEDs

Lifang Yuan,Yahong Jin,Guangting Xiong,Haoyi Wu,Jiacheng Li,Hai Liu,Li Chen,Yihua Hu

DOI: https://doi.org/10.1016/j.jallcom.2021.159394

IF: 6.2

2021-07-01

Journal of Alloys and Compounds

Abstract:Rare-earth free ions, especially Mn4+, doped phosphors with red emission have become a research hotspot. To achieve high-performance phosphor-converted warm w-LEDs, blue light activable Mn4+-doped phosphors with broadband red emission rather than the commonly sharp ones are highly desired. In this work, we report a novel Mn4+-doped Li2Mg3TiO6 phosphor prepared by the conventional solid-state reaction and the synthesis temperature is remarkably lowered from 1300 °C to 950 °C with the addition of LiF flux. The fluorescence properties were well characterized by steady and transient state spectroscopies. The occupation of Mn4+ ions for the center of octahedral sites leads to a blue light excitable phosphor showing unusual broadband deep-red emission. The addition of LiF enhances the Mn4+ emission intensity and 0.1 mol% Mn4+-doped phosphor attains the highest red emission intensity with the maximum PLQY = 35.1%. The Mn4+ emission presents good thermal resistance demonstrated by high-temperature dependent fluorescence and activation energy ΔE = 0.369 eV. The as-obtained red phosphor enables the fabrication of a warm w-LED device by the combination of commercial YAG yellow phosphor and blue LED (BLED) chip, giving CIE(x, y) = (0.307, 0.337), CRI = 83.9 and CCT = 5258 K. This work provides a promising candidate Li2Mg3TiO6:Mn4+ as broadband deep-red phosphor for warm w-LEDs as well as a method to effectively lower the preparation temperature.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
Insight into a Novel Rare-Earth-free Red-Emitting Phosphor Li3Mg2NbO6:Mn4+: Structure and Luminescence Properties

Xicheng Wang,Xiaopeng Zhou,Yaxin Cao,Qi Wei,Zhengyan Zhao,Yuhua Wang

DOI: https://doi.org/10.1111/jace.16527

IF: 4.186

2019-01-01

Journal of the American Ceramic Society

Abstract:Red phosphor is indispensable to achieve warm white light in the white light diode (WLED) application. However, the current red phosphors suffer from high cost and harsh synthesis conditions. In this study, an oxide-based rare-earth-free red-emitting phosphor Li3Mg2NbO6:Mn4+ (LMN:Mn4+) has been successfully synthesized by a simple solid-state reaction method. The relationship between crystal structure and luminescence was investigated in detail. The site occupancy of the doping Mn4+ ion in the LMN host has been discussed from the point of bond valence sum. How the coordination environment of doping Mn4+ affects the energy level of doping Mn4+ ion has been illustrated via the Tanabe-Sugano energy-level diagram. Moreover, warm white light has been obtained using LMN:Mn4+ as compensator to the YAG:Ce3+.
Synthesis, optical characteristics and thermal stability of Mn4+-doped Na3GaF6 red-emitting phosphor for high-performance warm WLED

Yuchen Tao,Yunfang Bai,Long Li,Junze Tong,Jingjing Zhang,Yuting Xu,Hai Lin,Feng Hong

DOI: https://doi.org/10.1016/j.molstruc.2023.137237

IF: 3.841

2024-03-01

Journal of Molecular Structure

Abstract:Nowadays, Mn4+-activated fluoride red phosphors with high color purity, strong zero phonon line emission and relatively short decay time are crucial for improving the optical performance of WLED and emerging applications. In this work, a series of red-emitting Mn4+-activated fluoride phosphors in consideration of the non-equivalent substitution of Mn4+ for Ga3+ in the Na3GaF6 host are synthesized via the coprecipitation method at room temperature. The use of different reaction solvents successfully regulates the morphology, size and luminescence intensity of the phosphor. Under blue light excitation, Na3GaF6:Mn4+ sample shows a bright narrow-band red emission with exceptional correlated color temperature (4029 K). Moreover, the emission of strong zero phonon line induces the outstanding color purity of red light (93%). In addition, the critical concentration of Mn4+ is determined to be 0.04 and the concentration quenching mechanism is also systematically discussed. Noticeably, when Na3GaF6:Mn4+ phosphor achieves maximum fluorescence emission, its fluorescence lifetime value is only 3.48 ms. Additionally, the theoretical calculated results demonstrate that Na3GaF6 host can provide strong crystal field strength for Mn4+, and the Racah parameters (B and C) and nephelauxetic ratio (β 1) are used to evaluate the nephelauxetic effect of Mn4+, which is compared with other types of Mn4+-activated phosphors. The activation energy, chromaticity shift and chromaticity coordinate variation are systematically calculated to analyze the thermal stability of Na3GaF6:Mn4+ red phosphor. Meanwhile, by employing the as-prepared phosphor Na3GaF6:Mn4+ as a red component, a high-performance warm WLED shows a full spectrum emission, and the corresponding cold white light emission is also transformed into the warm white light emission (CCT = 4224 K, Ra = 89.1 and LE = 111.72 lm/W). Moreover, under high driving current, such WLED exhibits stable output light efficiency. These results suggest that Na3GaF6:Mn4+ as red phosphor has a stupendous potential for warm WLED in indoor lighting.

chemistry, physical
Synthesis of an efficient Mn4+-doped fluoride red phosphor with excellent fluorescence stability by green synthesis method for warm WLED

Fengxi Hu,Yizheng Hu,Junze Tong,Long Li,Feng Hong,Jingjing Zhang,Yuting Xu,Hai Lin

DOI: https://doi.org/10.1016/j.optmat.2023.114129

IF: 3.754

2023-08-01

Optical Materials

Abstract:Currently, Mn4+-doped fluoride phosphors have become a research hotspot, which can help compensate for the missing red component in cold white light-emitting diodes (WLEDs). However, significant synthesis defects limit the development of such fluorescent powders due to the use of highly toxic solvent HF. To improve this situation, a simple green synthesis method should be explored to synthesize Mn4+-activated fluoride phosphor. In this study, a series of red-emitting Mn4+-activated BaTiF6 phosphors are successfully synthesized via the non-toxic reaction system (HNO3/HCl + NH4F). Its crystal structure, morphology, optical characteristics and thermal stability are systematically evaluated. Under blue light excitation, BaTiF6:Mn4+ exhibits a bright narrow-band red emission with exceptional correlated color temperature (3909 K) and color purity (90%). Additionally, the critical concentration of Mn4+ is determined to be 0.03 and the concentration quenching mechanism is also systematically discussed. By calculating the crystal field strength (D q), Racah parameters (B and C) and nephelauxetic effect ratio parameter β 1, it is confirmed that BaTiF6 host can provide a strong crystal field environment for Mn4+. Moreover, these results are compared with other matrix materials. Intriguingly, the optimal sample exists satisfactory thermal stability, whose fluorescence intensity at 423 K retains 49% of that at 298 K and the activation energy reaches up to 0.925 eV. In addition, the chromaticity shift and chromaticity coordinate variation are calculated as 17 × 10−3 and (−0.0063, 0.0063), respectively. Meanwhile, the feasibility of the as-fabricated WLEDs for interior illumination is examined. A high-performance warm WLED with low correlated color temperature (CCT = 4470 K) and high color rendering index (Ra = 88.3) is achieved by using BaTiF6:Mn4+ as a red-emitting material, moreover, WLED exhibits strong output stability under high driving current. The findings of this work provide a comprehensive understanding for rational design of high-performance Mn4+-activated fluoride red phosphors through a simple green synthesis method.

materials science, multidisciplinary,optics
Microsized Red Luminescent MgAl 2 O 4 :Mn 4+ Single-Crystal Phosphor Grown in Molten Salt for White LEDs

Zhaowu Wang,Haipeng Ji,Jian Xu,Xinghui Hou,Jumpei Ueda,Setsuhisa Tanabe,Shasha Yi,Ying Zhou,Deliang Chen

DOI: https://doi.org/10.1021/acs.inorgchem.0c03005

IF: 4.6

2020-11-27

Inorganic Chemistry

Abstract:A single-crystalline defect-less phosphor is desired for efficient luminescence of the therein doped optical activators. In this paper, microsized MgAl2O4:Mn4+ single-crystal phosphors with bright red luminescence were grown in molten LiCl salt at 950 °C, for application in blue LED pumped white lighting. By comparing the phosphor formation from various Mg2+- and Al3+-bearing sources, both the template-formation and the dissolution-diffusion processes were evidenced to account for the formation of the microsized MgAl2O4:Mn4+ crystallites. Using nano γ-Al2O3 as the Al3+-bearing precursor, the uniform MgAl2O4:Mn4+ microcrystallites with a {111} planes-exposed tetragonal bipyramid morphology were obtained. The photoluminescence property was studied at various temperatures, and Mg ↔ Al anti-site disorder induced luminescence broadening was discussed. The Mn4+2Eg → 4A2g transition in MgAl2O4 shows a quite short luminescence wavelength peaking at 651 nm and ultrabroadband emission extending to 850 nm. The luminescence is relatively robust against thermal effect with relatively high thermal quenching temperature of 400 K and activation energy of 0.23 eV. Employing the red-emitting MgAl2O4:Mn4+ crystallites, blue LED pumped white lighting prototypes were fabricated which simulate the solar-like spectrum and show neutral to warm white.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.inorgchem.0c03005?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.inorgchem.0c03005</a>.Evaluation of the LiCl volatilization, XRD patterns and PLE spectra of the MgAl2O4:Mn4+ synthesized under various conditions, SEM image, CIE 1931 diagram, deconvolution of the PLE spectrum, quantum yield measurement, and color rendering of the white LEDs (<a class="ext-link" href="/doi/suppl/10.1021/acs.inorgchem.0c03005/suppl_file/ic0c03005_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

chemistry, inorganic & nuclear
Orderly-layered tetravalent manganese-doped strontium aluminate Sr 4 Al 14 O 25: Mn 4+: An efficient red phosphor for warm white light emitting diodes

Mingying Peng,Xuewen Yin,Peter A. Tanner,Chuqi Liang,Pengfei Li,Qinyuan Zhang,Jianrong Qiu

DOI: https://doi.org/10.1111/jace.12391

IF: 4.186

2013-01-01

Journal of the American Ceramic Society

Abstract:Searching for an efficient non rare earth-based oxide red phosphor, particularly excitable by light in the wavelength from 380 to 480nm and unexcitable by green light, is essential for the development of warm white light emitting diodes (WLEDs). Here, we report a promising and orderly-layered candidate: Sr4Al14O25:Mn4+ with CIE color coordinates (0.722, 0.278). It has higher luminescence efficiency particularly upon blue excitation and is much cheaper than the commercial red phosphor 3.5MgO<bold>0</bold>.5MgF2GeO2:Mn4+ (MMG:Mn4+). In sharp contrast to Eu2+-doped (oxy)nitrides, the phosphor can be synthesized by a standard solid-state reaction at 1200 degrees C in air. The effects of flux boron content, environment, and preparation temperature, sintering dwelling time as well as Mn concentration have been systematically investigated for establishing the optimal synthesis conditions. The low temperature emission spectra reveal that there are at least three types of Mn4+ ions in Sr4Al14O25:Mn4+ due to the substitution for the distorted octahedral Al3+ sites. The AlO6 layers where Mn4+ prefers to reside are well separated from one another by AlO4 tetrahedra in one dimension parallel to axis a. This scenario can efficiently isolate Mn4+ ions from local perturbations, thereby enabling the high efficiency of luminescence. The energy transfer rates and mechanism are discussed.
Orderly‐Layered Tetravalent Manganese‐Doped Strontium Aluminate Sr4Al14O25:Mn4+: an Efficient Red Phosphor for Warm White Light Emitting Diodes

Mingying Peng,Xuewen Yin,Peter A. Tanner,Chujun Liang,Pengfei Li,Qinyuan Zhang,Jianrong Qiu

DOI: https://doi.org/10.1111/jace.12391

IF: 4.186

2013-01-01

Journal of the American Ceramic Society

Abstract:Searching for an efficient non rare earth‐based oxide red phosphor, particularly excitable by light in the wavelength from 380 to 480 nm and unexcitable by green light, is essential for the development of warm white light emitting diodes ( WLED s). Here, we report a promising and orderly‐layered candidate: Sr 4 Al 14 O 25 : Mn 4+ with CIE color coordinates (0.722, 0.278). It has higher luminescence efficiency particularly upon blue excitation and is much cheaper than the commercial red phosphor 3.5 MgO ·0.5 MgF 2 · GeO 2 : Mn 4+ ( MMG : Mn 4+ ). In sharp contrast to Eu 2+ ‐doped (oxy)nitrides, the phosphor can be synthesized by a standard solid‐state reaction at 1200°C in air. The effects of flux boron content, environment, and preparation temperature, sintering dwelling time as well as Mn concentration have been systematically investigated for establishing the optimal synthesis conditions. The low temperature emission spectra reveal that there are at least three types of Mn 4+ ions in Sr 4 Al 14 O 25 : Mn 4+ due to the substitution for the distorted octahedral Al 3+ sites. The AlO 6 layers where Mn 4+ prefers to reside are well separated from one another by AlO 4 tetrahedra in one dimension parallel to axis a . This scenario can efficiently isolate Mn 4+ ions from local perturbations, thereby enabling the high efficiency of luminescence. The energy transfer rates and mechanism are discussed.
Novel Mn4+-activated fluoride red phosphors induced by alkaline metal ions replacement: Green synthesis, luminescence enhancement, high stability and application in warm WLED

Junze Tong,Long Li,Haiqing Su,Feng Hong,Edwin Yue Bun Pun,Hai Lin

DOI: https://doi.org/10.1016/j.ceramint.2023.08.295

IF: 5.532

2023-08-01

Ceramics International

Abstract:Red-emitting Mn4+-doped fluoride phosphors are promising fluorescent material for use in high-performance warm white light emitting diodes (WLEDs). However, Low stability and non-green synthesis method limit the development and commercialization of such phosphor. Herein, a series of novel (Li/Na/Cs)0.4Ba0.8SiF6:Mn4+ phosphors with optimized fluorescence properties induced by alkaline metal ions replacement are successfully synthesized via a green and eco-friendly approach. Under the irradiation of 460 nm blue light, Cs0.4Ba0.8SiF6:Mn4+ red phosphor with narrow band emission peak has the best optical performance. The optimal doping concentration of Mn4+ in Cs0.4Ba0.8SiF6 host and the reason for concentration quenching are systematically analyzed. Furthermore, the moisture resistance and thermal stability of this phosphor are discussed. After being soaked in deionized water for 90 min, the PL intensity of Cs0.4Ba0.8SiF6:Mn4+ phosphor can maintain at 40% of that in air, which is 4 times higher than commercial K2SiF6:Mn4+. At the operating temperature of LED (423 K), Cs0.4Ba0.8SiF6:Mn4+ red phosphor can exhibit stable light output intensity and color. A warn WLED with low correlated color temperature of 4336 K, high color rendering index of 88.4 and high lumen efficiency of 105.96 lm/W is fabricated via using Cs0.4Ba0.8SiF6:Mn4+ phosphor as a component of red-light, and the warm WLED can maintain stable output even at high driving currents. Overall, the alkali metal ion replacement and green synthesis strategies have opened up a new perspective for the synthesis of efficient Mn4+-doped fluoride phosphors, which has dual benefits for optimizing the performance of WLED and environmental protection.

materials science, ceramics
Green synthesis, luminescent properties and application for WLED of flower-like K2LiAlF6:Mn4+ phosphor

Xiaoyi Liu,Haiping Xu,Yunxiao Zhang,Zhendong Fu,Feng Hong,Ge Pang,Guixia Liu,Dan Li,Xiangting Dong,Jinxian Wang

DOI: https://doi.org/10.1016/j.optmat.2021.111392

IF: 3.754

2021-09-01

Optical Materials

Abstract:Chrysanthemum-like K2LiAlF6:Mn4+ phosphors were synthesized by simple co-precipitation method without using HF. The K2LiAlF6:Mn4+ phosphor can be effectively excited through blue light at 465 nm, then produces sharp red-light emission near 634 nm. The luminescence quenching of Mn4+ is caused by the d-d interaction between Mn4+ ions. The effects of surfactant and lithium source on the luminescent properties of K2LiAlF6:Mn4+ phosphors were discussed. Mn4+ is located in a strong crystal field environment in the K2LiAlF6 matrix and its emission mechanism is discussed. Warm white light emitting diode (WLED) device, which is fabricated by coating a certain proportion mixture of yellow YAG:Ce3+ phosphor and red K2LiAlF6:5%Mn4+ phosphor on the blue GaN chip, has low correlation color temperature (CCT = 3588 K), high color rendering index (Ra = 90.8) and good electroluminescence stability under different currents. These properties illustrate that K2LiAlF6:5%Mn4+ phosphor is a promising red light emitting material.

materials science, multidisciplinary,optics
Synthesis, Structure and Luminescence Properties of Mn-doped MgAl2O4 Red-Emitting Phosphors with Varying Sintering Temperature

Jiahao Zha,Chongjun He,Fangzhou Chen,Hongwei Wang,Biao Dong,Lijuan Liu,Mingjun Xia,Chenguang Deng,Qian Li,Yuangang Lu,Huiting Chen

DOI: https://doi.org/10.1007/s10895-024-03937-w

2024-09-27

Journal of Fluorescence

Abstract:Oxide matrix red-emitting phosphors are deemed as excellent color converters for white light emitting diodes (WLEDs) and laser diodes (LDs). Manganese-doped MgAl 2 O 4 powder was synthesized by a solid-state reaction method at different sintering temperatures. Microstructure shows that grain size is mainly in the range of 0.2–5 μm, and grain agglomeration occurs with increased sintering temperature. XPS analysis indicates that the doped Mn ion exhibits a valence state of + 4 within the MgAl 2 O 4 matrix. The diffraction peak of the phosphors is shifted by the sintering temperature, which affects lattice constant. Upon excitation by 300 nm ultraviolet light, the samples emit asymmetric broadband red light within the range of 620–720 nm, attributed to Mn 4+ ion's transition from 2 E g to 4 A 2g states. With the increasing temperature, the main emission peak shifts from 677 nm to 650 nm, ascribed to the change in energy level ( 2 E g ) resulting from the reduction of Al 2 O 3 phase. Crystal field theory confirmed that Mn 4+ ions are within a strong crystal field environment created by MgAl 2 O 4 matrix. By affecting particle size and crystallinity, the sintering temperature influences the fluorescence lifetime of the Mn 4+ ion. Notably, these red-emitting phosphors exhibits remarkable thermal stability as their emission intensity remains approximately at 58% of initial intensity even at elevated temperature (435 K). Consequently, Mn 4+ : MgAl 2 O 4 red-emitting phosphors with high thermal stability render them promising candidates for WLED applications.

chemistry, physical, analytical,biochemical research methods
A novel inequivalent double-site substituted red phosphor Li 4 AlSbO 6 :Mn 4+ with high color purity: its structure, photoluminescence properties, and application in warm white LEDs

Zhiyuan Li,Xuhui Zhang,Ji Wu,Rui Guo,Lan Luo,Yuhua Xiong,Li Wang,Wei Chen

DOI: https://doi.org/10.1039/d1tc02541d

IF: 6.4

2021-01-01

Journal of Materials Chemistry C

Abstract:A novel inequivalent double-site substituted red phosphor Li 4 AlSbO 6 :Mn 4+ with high color purity for warm white LEDs.

materials science, multidisciplinary,physics, applied
High Efficiency Mn4+ Doped Sr2mgal22o36 Red Emitting Phosphor For White Led

Renping Cao,Mingying Peng,Enhai Song,Jianrong Qiu

DOI: https://doi.org/10.1149/2.022204jss

IF: 2.2

2012-01-01

ECS Journal of Solid State Science and Technology

Abstract:A novel high efficiency red emitting Sr2MgAl22O36:Mn4+ phosphor is synthesized by solid-state reaction method. The optimized red emitting Sr2MgAl22O36:Mn4+ phosphor exhibits high quantum efficiency (QE) of similar to 80%, fluorescence lifetime of similar to 1.25 ms and the Commission International de I'Eclairage (CIE) chromaticity coordinates (0.72, 0.27). The Sr2MgAl22O36:Mn4+ phosphor shows excitation bands at similar to 400 and 470 nm which matches well with working wavelength of existed LED chips can be used as excitation source to generate white emission. White LED was fabricated by using mixed phosphors Sr2MgAl22O36:Mn4+ and (Sr, Ba)(2)SiO4:Eu2+ (green emitting phosphor) excited with a 397 nm near UV-chip. (C) 2012 The Electrochemical Society.
Luminescence properties, crystal field and nephelauxetic effect on (NH4)2NaMF6: Mn4+ (M = Al, Ga and In) red phosphors for warm white light-emitting diodes

Hu Wang,Xiaoyi Liu,Feng Hong,Yunkai Dong,Yanan Li,Guixia Liu,Jinxian Wang,Dan Li,Wensheng Yu,Xiangting Dong

DOI: https://doi.org/10.1016/j.jlumin.2022.119242

IF: 3.6

2022-11-01

Journal of Luminescence

Abstract:In recent years, M (M = Al, Ga and In)-based fluoride red phosphors have received widespread attention. Herein, the red phosphors (NH4)2NaAlF6:Mn4+ (NNAFM), (NH4)2NaGaF6:Mn4+ (NNGFM) and (NH4)2NaInF6:Mn4+ (NNIFM) were synthesized by hydrothermal method, and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy-dispersive X-ray spectrometers (EDS). Upon 470 nm light irradiation, the strongest emission peaks of (NH4)2NaMF6:Mn4+ red phosphors were at 637 nm (NNAFM), 636 nm (NNGFM) and 634 nm (NNIFM), respectively. This blue shift phenomenon with the increase of atomic radius was analyzed by crystal field and nephelauxetic effect. Besides, the concentration quenching mechanism, fluorescence lifetime and thermal stability were also discussed. Finally, three kinds of red phosphors were combined with blue chip and yellow phosphor (YAG:Ce3+) to form LED devices for improving their performance. The LED device (blue chip-YAG:Ce3+-NNGFM) possesses high color rendering index (Ra = 90.1), low correlated color temperature (3422 K) and luminous efficiency (41.23 lm W−1).

optics
Crystal field optimization and fluorescence enhancement of Mn4+-doped fluoride red phosphor with excellent stability induced by double-site metal ion replacement for warm WLED

Junze Tong,Feng Hong,Long Li,Edwin Yue Bun Pun,Hai Lin

DOI: https://doi.org/10.1039/d3dt01239e

IF: 4

2023-06-15

Dalton Transactions

Abstract:The effective double-site metal ion replacement strategy is adopted to optimize the crystal field environment of Mn4+-activated fluoride phosphor. In this work, a series of K2yBa1-ySi1-xGexF6:Mn4+ phosphors with optimized fluorescence intensity, excellent water resistance and outstanding thermal stability have been synthesized. The composition adjustment includes two different types of ion substitution based on BaSiF6:Mn4+ red phosphor: [Ge4+→Si4+] and [K+→Ba2+]. X-ray diffraction and theoretical analysis reveal that Ge4+ and K+ can be successfully introduced into BaSiF6:Mn4+ to form new solid solution K2yBa1-ySi1-xGexF6:Mn4+ phosphors. The emission intensity enhancement and slight wavelength shift are detected in different cation replacement procedures. Furthermore, K0.6Ba0.7Si0.5Ge0.5F6:Mn4+ with superior color stability performance has a negative thermal quenching phenomenon. Excellent water resistance is also found, which is more reliable than K2SiF6:Mn4+ commercial phosphor. Warm WLED with low correlated color temperature (CCT = 4000 K) and high color rendering index (Ra = 90.6) is successfully packaged by using K0.6Ba0.7Si0.5Ge0.5F6:Mn4+ as the red light component, and it also exhibits high stability for different currents. These findings demonstrate that the effective double-site metal ion replacement strategy can open up a new avenue for designing new Mn4+-doped fluoride phosphor to improve the optical properties of WLED.

chemistry, inorganic & nuclear
Designed synthesis, morphology evolution and enhanced photoluminescence of a highly efficient red dodec-fluoride phosphor, Li3Na3Ga2F12:Mn4+, for warm WLEDs

Jun Lin,Mengmeng Zhu,Hongzhou Lian,Yuexiao Pan,Ya-shih Huang

DOI: https://doi.org/10.1039/C7TC04878E

2018-01-18

Abstract:Red phosphors of the Mn4+ doped dodec-fluoride Li3Na3Ga2F12:Mn4+ (LNGF:Mn) with various morphologies have been synthesized from K2MnF6, LiF, NaF and Ga2O3 in HF at room temperature with excess LiF and NaF relative to the stoichiometric composition of LNGF:Mn. The formation mechanism of the red phosphor LNGF:Mn has been discussed based on detailed experimental results compared with that of the identified phosphor Li3Na3Al2F12:Mn4+ (LNAF:Mn). The optical properties of LNGF:Mn have been systematically investigated and compared with those of red phosphors Li3GaF6:Mn4+ (LGF:Mn), Na3GaF6:Mn4+ (NGF:Mn) and LNAF:Mn in detail. It is observed that the as-obtained phosphor LNGF:Mn exhibits superior properties in chromaticity coordinates as well as a high luminescence efficiency with a strong potential to enhance the performance of solid-state lighting. The HF-concentration-dependent morphologies of the phosphor LNGF:Mn have been investigated by scanning electron microscopy (SEM). The luminescence of the phosphor LNGF:Mn has been enhanced by optimizing the synthetic parameters, such as the concentrations of HF and K2MnF6. The white light-emitting diode (WLED) encapsulated with the as-obtained red phosphor LNGF:Mn and a commercial yellow one, Y3Al5O12:Ce3+ (YAG:Ce), on a GaN chip produces a warm white light with a color rendering index (CRI) of 91.32 at a correlated color temperature (CCT) of 3986.08 K.

Physics,Materials Science
Temperature Dependent Red Luminescence From A Distorted Mn4+ Site In Caal4o7:Mn4+

Pengfei Li,Mingying Peng,Xuewen Yin,Zhijun Ma,Guoping Dong,Qinyuan Zhang,Jianrong Qiu

DOI: https://doi.org/10.1364/OE.21.018943

IF: 3.8

2013-01-01

Optics Express

Abstract:Thermal luminescence quenching behavior of a phosphor is essential for application in phosphor converted white light emitting diodes (pc-WLEDs) because the phosphor layer can be heated up to 473K in a working high power WLEDs. Here, we have confirmed indeed a red luminescence of Mn4+ substituting for calcium sites rather than tetrahedral aluminum sites in CaAl4O7:Mn which can be synthesized in pure phase even with boron acid as flux, and examined the low and high temperature luminescent properties in the range of 10 to 500K. We have revealed as well as thermal quenching mechanism that distorted octahedral Mn4+ sites suffer severe thermal quenching. This work, thus, hints a strategy to find a new Mn4+ phosphor with better resistance to thermal impact in the future. (c) 2013 Optical Society of America
Highly Regular, Uniform K3ScF6:Mn4+ Phosphors: Facile Synthesis, Microstructures, Photoluminescence Properties, and Application in Light-Emitting Diode Devices

Hong Ming,Shuifu Liu,Lili Liu,Jiaqing Peng,Junxiang Fu,Fu Du,Xinyu Ye

DOI: https://doi.org/10.1021/acsami.8b01885

2018-06-13

Abstract:A new generation of red phosphors of complex fluoride matrices activated with Mn4+ has gained a broad interest in getting high color quality and low color temperature of solid-state white light-emitting diodes (WLEDs). However, besides their instability toward moisture, the extremely irregular and nonuniform morphologies of these phosphors have limited their practical industry applications. In the present study, a novel type of K3ScF6:Mn4+ red phosphor with highly regular, uniform, and high color purity was obtained successfully through a facile coprecipitation route under mild conditions. The crystal structure was identified with aids of the powder X-ray diffraction, Rietveld refinement, and density functional theory calculations. The prototype crystallizes in the space group Fm3 m with a cubic structure, and the lattice parameters are fitted well to be a = b = c = 8.4859(8) Å and V = 611.074(2) Å3. The Mn4+ ions occupy Sc3+ sites and locate at the centers of the distorted ScF6 octahedrons. A wide band gap of approximately 6.15 eV can provide sufficient space to accommodate impurity energy levels. Unlike most other Mn4+ ion-activated fluoride phosphors, the as-prepared K3ScF6:Mn4+ phosphors demonstrate highly uniform and regular morphologies with shapes transforming from cube to octahedron with increasing Mn4+ ion concentration. Under blue light excitation, the as-prepared K3ScF6:Mn4+ sample exhibits intense sharp-line red fluorescence (the strongest peak located at 631 nm) with high color purity. An excellent recovery in luminescence upon heating and cooling processes implies high stability of K3ScF6:Mn4+. Furthermore, a warm WLED fabricated with blue GaN chips merged with the mixture of K3ScF6:Mn4+ and the well-known commercial YAG:Ce3+ yellow phosphors exhibits wonderful color quality with lower correlated color temperature (3250 K) and higher color-rendering index ( Ra = 86.4). These results suggest that the K3ScF6:Mn4+ phosphor possesses stupendous potentiality for practical applications.
High Performance Sr4Al14O25:Mn4+ Phosphor:Structure calculation and Optical properties

Xingsen Wang,Quan Jiang,Zixiang Wang,Biqing Song,Hailan Hou,Liang Xu,LiBin Xia,xingsen wang,quan jiang,zixiang wang,biqing song,hailan hou,Libin Xia

DOI: https://doi.org/10.1039/d2tc00795a

IF: 6.4

2022-01-01

Journal of Materials Chemistry C

Abstract:The deficiency of high optical performance oxide red phosphor limits the application and development in the field of warm WLEDs. In this work. Sr4Al14O25:Mn4+ (SAO:Mn4+) series oxide red phosphors efficiently...

materials science, multidisciplinary,physics, applied

Mn<sup>4+</sup> nonequivalent-doped Al<sup>3+</sup>-based cryolite high-performance warm WLED red phosphors

Synthesis and luminous characteristics of Ba2MgSi2-xAlxO7: 0.1Eu2+, 0.1Mn2+ phosphor for WLED

Monodisperse CaAl12O19:Mn4+ Microspheres for Full-Spectrum White LEDs

Flux-assisted low-temperature synthesis of Mn4+-doped unusual broadband deep-red phosphors toward warm w-LEDs

Insight into a Novel Rare-Earth-free Red-Emitting Phosphor Li3Mg2NbO6:Mn4+: Structure and Luminescence Properties

Synthesis, optical characteristics and thermal stability of Mn4+-doped Na3GaF6 red-emitting phosphor for high-performance warm WLED

Synthesis of an efficient Mn4+-doped fluoride red phosphor with excellent fluorescence stability by green synthesis method for warm WLED

Microsized Red Luminescent MgAl 2 O 4 :Mn 4+ Single-Crystal Phosphor Grown in Molten Salt for White LEDs

Orderly-layered tetravalent manganese-doped strontium aluminate Sr 4 Al 14 O 25: Mn 4+: An efficient red phosphor for warm white light emitting diodes

Orderly‐Layered Tetravalent Manganese‐Doped Strontium Aluminate Sr4Al14O25:Mn4+: an Efficient Red Phosphor for Warm White Light Emitting Diodes

Novel Mn4+-activated fluoride red phosphors induced by alkaline metal ions replacement: Green synthesis, luminescence enhancement, high stability and application in warm WLED

Green synthesis, luminescent properties and application for WLED of flower-like K2LiAlF6:Mn4+ phosphor

Synthesis, Structure and Luminescence Properties of Mn-doped MgAl2O4 Red-Emitting Phosphors with Varying Sintering Temperature

A novel inequivalent double-site substituted red phosphor Li 4 AlSbO 6 :Mn 4+ with high color purity: its structure, photoluminescence properties, and application in warm white LEDs

High Efficiency Mn4+ Doped Sr2mgal22o36 Red Emitting Phosphor For White Led

Luminescence properties, crystal field and nephelauxetic effect on (NH4)2NaMF6: Mn4+ (M = Al, Ga and In) red phosphors for warm white light-emitting diodes

Crystal field optimization and fluorescence enhancement of Mn4+-doped fluoride red phosphor with excellent stability induced by double-site metal ion replacement for warm WLED

Designed synthesis, morphology evolution and enhanced photoluminescence of a highly efficient red dodec-fluoride phosphor, Li3Na3Ga2F12:Mn4+, for warm WLEDs

Temperature Dependent Red Luminescence From A Distorted Mn4+ Site In Caal4o7:Mn4+

Highly Regular, Uniform K3ScF6:Mn4+ Phosphors: Facile Synthesis, Microstructures, Photoluminescence Properties, and Application in Light-Emitting Diode Devices

High Performance Sr4Al14O25:Mn4+ Phosphor:Structure calculation and Optical properties