Abstract:A series of nanofibrous alumina materials with diameters of 4-6 nm and with different aspect ratios ranging from 3 to 16 were prepared. Cobalt impregnated catalysts were prepared by means of incipient wetness impregnation on alumina nanofibers while the 'rearranged' catalysts were prepared by using ultrasonication assistance to mix the fibers with the Co3O4 nanoparticles. The effects of the alumina nanofiber aspect ratios on the Co catalyst structure and performance for Fischer-Tropsch synthesis were studied. The pore size of the two series of catalysts increased as the aspect ratio of the alumina nanofiber increased. For impregnated catalysts, large Co3O4 particles were formed on the external surface of the alumina support when the aspect ratio was 3 and 5, while the crystallite sizes of Co3O4 increased from 13.3 nm to 15.6 nm with the increase of the aspect ratio from 7 to 16. The four 'rearranged' catalysts possessed similar and homogeneously dispersed Co3O4 crystallites of 9.5 nm. As expected the reduction behavior of the two series of catalysts was primarily influenced by the Co3O4 crystallite size and structure. The FT data of the two series of catalysts indicate that dispersed Co catalysts on alumina nanofibers with large aspect ratios having large inter-crystallite pores significantly improve the catalyst activity and C5+ selectivity. The FT data of the 'rearranged' catalysts strongly demonstrated that the internal mass transfer of reactants and products increased with a decrease in inter-crystallite pore size, resulting in a decrease of C5+ selectivity and C3 olefin/paraffin ratio, and an increase of CH4 selectively, while the CO consumption rate was little altered. Furthermore, catalytic stability tests showed that the alumina nanofibers with larger aspect ratios inhibited Co migration and coalescence in the matrices of the nanofibrous alumina, and this significantly enhanced the stability of the catalyst. The Cop/Al2O3-16 catalyst possessing uniformly distributed cobalt, improved reducibility and large pores is the preferred choice to generate high catalytic activity, stability and C5+ selectivity.

Nanofibers and amorphous Ni/Al<sub>2</sub>O<sub>3</sub> catalysts — effect of steric hindrance on hydrogenation performance

Nanofibers and amorphous Ni/Al2O3 catalysts — Effect of steric hindrance on hydrogenation performance

Investigation on the structure and performance of supported Ni nanoparticles for the hydrogenation of furfural

Selective hydrogenation of furfural and its derivative over bimetallic NiFe-based catalysts: Understanding the synergy between Ni sites and Ni–Fe alloy

Novel Mesoporous Ag@SiO2 Nanospheres As a Heterogeneous Catalyst with Superior Catalytic Performance for Hydrogenation of Aromatic Nitro Compounds

Carbon-Embedded Ni Nanocatalysts Derived from Mofs by A Sacrificial Template Method for Efficient Hydrogenation of Furfural to Tetrahydrofurfuryl Alcohol

Nanocatalysts Anchored on Nanofiber Support for High Syngas Production Via Methane Partial Oxidation

The Effect of the Nanofibrous Al2O3 Aspect Ratio on Fischer-Tropsch Synthesis over Cobalt Catalysts.

Hydrogenation of fatty acids to fatty alcohols over Ni 3 Fe nanoparticles anchored on TiO 2 crystal catalyst: Metal support interaction and mechanism investigation

Supported Ultrafine NiCo Bimetallic Alloy Nanoparticles Derived from Bimetal–Organic Frameworks: A Highly Active Catalyst for Furfuryl Alcohol Hydrogenation

Importance of oxyphilic FeNi alloy in NiFeAl catalysts for selective conversion of biomass-derived 5-hydroxymethylfurfural to 2,5-dimethylfuran

Hierarchically Nitrogen‐doped Porous Carbon‐Supported Non‐noble Metal Nanoparticles for Promoting the Selective Hydrogenation of Furfural

Fluorinated Cu/Zn/Al/Zr Hydrotalcites Derived Nanocatalysts for CO2 Hydrogenation to Methanol

Trimetallic NiZr/CoOx catalyst for the selective hydrogenation of furfural into furfuryl alcohol

Enhanced stability for chemoselective hydrogenation of Nitroarenes by carbon layer coated Ni‐Fe alloy catalyst

Advances in Studies of Structural Effect of the Supported Ni Catalyst for CO2 Hydrogenation: from Nanoparticle to Single Atom Catalyst

Selective Hydrogenation of Furfural over Pt Based and Pd Based Bimetallic Catalysts Supported on Modified Multiwalled Carbon Nanotubes (MWNT)

The catalytic hydrogenation of furfural to 2-methylfuran over the Mg-Al oxides supported Co-Ni bimetallic catalysts

Assembling Co clusters via nanosized ZIF-67 sprouted from CoAl-LDH nanoflower for selective hydrogenation

Nanocrystalline Iron–boron Catalysts for Low-Temperature CO Hydrogenation: Selective Liquid Fuel Production and Structure–activity Correlation

Hydrophobic Nanosized H-Beta Catalysis for Biomass Furanic Compound Valorization