Abstract:Cu and unoxidized graphene composite films were prepared by electroplating under room temperature. Graphene was added to the electrolyte of Cu to form composite materials to improve the performance of Cu for interconnection. Composite electrolyte containing high concentration of graphene (up to 0.5 g/L) was prepared by adding CTAB as surfactant. And ultrasound was also used to increase dispersion degree and reduce graphene agglomeration in electrolyte. Average coefficient of thermal expansion (CTE) of the composite films determined by thermo-mechanical analysis (TMA) shows a decrease from 17.3 ppm/K to 14.2 ppm/K from 260 K to 320 K, which reduce CTE by 18 % compared with Cu. CTE of the composite materials can be reduced to 10 ppm/K at 243 K, which is only 60 % of CTE of Cu. The thermal conductivity of the composite materials measured by phase sensitive transient thermo-reflectance (PSTTR) technique shows an improvement from 385 W/m.K to 468 W/m.K. CTE and thermal conductivity of the composite materials both decrease with the increase of current density. And they also both increase with the increase of graphene concentration. The composite materials also show good mechanical properties. The average hardness is 2.5 GPa, which is about 2 times of Cu. And the average elastic modulus is 145 GPa, which is 38 % higher than that of Cu. The resistivity of the composite materials is basically equivalent to that of pure Cu. Result of the experiment proved that the composite materials have better performance under low temperature conditions. The improvement of material properties makes composite materials have good application prospects for 3D interconnection in the near future.

Characterization of Graphene Based Conductive Paste

Praparation, Characterizations, and Its Potential Applications of PANi/ Graphene Oxide Nanocomposite

Waterborne conductive carbon paste with an eco-friendly binder

Unveiling the Thickness-Dependent Mechanical Properties of Graphene Papers by in Situ SEM Tension.

Preparation of Functionalized Graphene/thermal Conductive Polyurethane Films

Preparation of waterborne graphene paste with high electrical conductivity

Fabrication and investigation of a new copper-doped screen-printable carbon paste's conductive mechanism by AFM

Research on the Characteristics of Graphene-metal Contact

Synthesis and Characterization of Graphene Nanoplatelets Fabricated by Electrochemical Exfoliation Method for Conductive Adhesive

High Quality and Large-Scale Manually Operated Monolayer Graphene Pasters

Preparation and Application of Carbon-Based Conductive Ink Based on Graphene

Foundation Froperties of Graphite Filled Cement Conductive Composites

Investigation on the Poor Fluidity of Electrically Conductive Cement-Graphite Paste: Experiment and Simulation

Preparation and Characterization of Electroplated Cu/Graphene Composite

Characterization of a Hybrid Cu Paste as an Isotropic Conductive Adhesive

Highly electrically conductive polyether composites with modified graphene

Synthesis and Properties of Non-Curing Graphene Thermal Interface Materials

Multifunctional, durable and highly conductive graphene/sponge nanocomposites

In Situ Synthesis of Silver/chemically Reduced Graphene Nanocomposite and Its Use for Low Temperature Conductive Paste

Characterization and Electrical Properties of Conductive Polymer/colloidal Graphite Oxide Nanocomposites