Coercivity and Thermal Stability Enhancement for Spark-Plasma-Sintered Nanocrystalline NdFeB Magnets With Dy₂O₃ and Zn Additions

Z. W. Liu,L. Z. Zhao,S. L. Hu,H. Y. Yu,X. C. Zhong,X. X. Gao

DOI: https://doi.org/10.1109/intmag.2015.7157718

IF: 1.848

2015-01-01

IEEE Transactions on Magnetics

Abstract:NdFeB bulk magnets were synthesized by spark plasma sintering (SPS) using the precursors of melt spun nanocrystalline Nd10.15Pr1.86Fe80.41Al1.67B5.91 ribbons mixed with Zn and/or Dy2O3 powders. The addition of 0.6 wt.% Zn or 2 wt.% Dy2O3 is effective in improving the magnetic properties of the magnets, and their coercivities are about 11% or 15%, respectively, higher than that of the additive free magnet. Both additives can suppress the grain growth of Nd2Fe14B phase. Dy2O3 is not beneficial to the densification during SPS, but Dy is considered to partly diffuse into the grains near particle boundaries and to form (Nd, Dy)2Fe14B phase. NdZn and NdZn5 phases were observed in the SPSed magnets with Zn additions more than 1 wt.%, which leads to coarse grains and porosities between the particles. The magnet with combined additions of 2 wt.% Dy2O3 and 0.6 wt.% Zn showed good thermal stability with small temperature coefficients and optimal magnetic properties with high coercivity and maximum energy product.