Magnetostriction “drop” in 〈110〉 Oriented Polycrystals Tb0.36Dy0.64(Fe0.85Co0.15)2 after Transverse Field Annealing

Changsheng Zhang,Tianyu Ma,Mi Yan

DOI: https://doi.org/10.1063/1.3563078

IF: 2.877

2011-01-01

Journal of Applied Physics

Abstract:A 〈110〉 oriented polycrystal Tb0.36Dy0.64(Fe0.85Co0.15)2 was subjected to annealing in a transverse field of 240 kA/m. Axial magnetostrictions (defined as λ∥) of the magnetically annealed specimen were investigated in fields applied at a series of angles θ away from its axis. For the untreated specimen, at the angle θ scope from 30° to 60°, λ∥ increases to a maximum and then drops gradually during magnetization processes. After magnetic annealing, however, the magnetostriction “drop” behavior occurs at a narrower θ range from 40° to 60°. In addition, at these magnetization directions where drop occurs, λ∥ is negative for the magnetically annealed specimen, whereas it keeps positive for the untreated one. The value of “dropped” magnetostriction (defined as |Δλ∥,d|) increases with the increase of θ for the untreated specimen, but decreases for the magnetically annealed one. Based on a single-{111}-twin crystal growth model, magnetic domain rotation paths are simulated to explain the differential magnetostriction drop behavior.