Abstract:NaMgH3 has been considered to be a potential candidate for solid-state hydrogen storage due to its considerable hydrogen gravimetric (6.0 wt %) and volumetric (88.0 g/L) densities. Meanwhile, NaMgH3 possesses an outstanding theoretical thermal storage density of 2881 kJ/kg, which makes it one of the most promising thermal energy storage materials. However, the sluggish dehydrogenation kinetics of NaMgH3 embarrasses further practical application. Doping a nanosize Ti-based catalyst is treated to be one of the most effective methods to settle the poor dehydriding kinetics. In this work, different kinds of TiO2 catalysts, the 5 wt % TiO2 microparticle (MP) (100 nm), TiO2 nanoparticle (NP) (5-10 nm), and TiO2 nanotube (NT) (5-10 nm), were doped into NaMgH3 in the process of ball milling and heat treatment, which in situ formed Na(0.4)6TiO(2) significantly promoting the full hydrogen desorption kinetics of NaMgH3. Among all samples, the TiO2 NT doped sample shows the best performance of which the onset decomposition temperature is reduced to 300 degrees C, and the first-and second-step decomposition peak temperatures are decreased to 346.3 and 355.8 degrees C, respectively. The TiO2 NT-doped sample desorbs approximately 3.4 wt % H-2 at 350 degrees C within 10 min, while the pure NaMgH3 sample releases only 0.2 wt % H-2 in 10 min. The significant improvement in both two decomposition reactions kinetics of NaMgH3 can be attributed to the tubular morphology of the TiO2 NT and the in situ formation of multivalence Ti species (Na0.46TiO2). These two reasons can change the kinetic models of NaMgH3 from A2 to R2 and further dramatically decrease the activation energies of first-and second-step decomposition reactions of NaMgH3 to 91.7 and 142.1 kJ/mol, respectively. In particular, the in situ formed Na0.46TiO2 can benefit the e-transfers among Na+, Mg2+, and H-, tremendously enhancing dehydrogenation properties.

Improved dehydrogenation of TiF<sub>3</sub>-doped NaAlH<sub>4</sub> using ordered mesoporous SiO<sub>2</sub> as a codopant

Improved Dehydrogenation Of Tif3-Doped Naalh4 Using Ordered Mesoporous Sio2 As A Codopant

Excellent Catalysis of Various TiO 2 Dopants with Na 0.46 TiO 2 in Situ Formedon the Enhanced Dehydrogenation Properties of NaMgH 3

Improved dehydrogenation/rehydrogenation performance of LiBH 4 by doping mesoporous Fe 2 O 3 or/and TiF 3

Remarkable Hydrogen Absorption/desorption Behaviors and Mechanism of Sodium Alanates In-Situ Doped with Ti-based 2D MXene

Sodium Alanate In-Situ Doped with Ti2C MXene with Enhanced Hydrogen Storage Properties

Excellent Catalysis of Various TiO<sub>2</sub> Dopants with Na<sub>0.46</sub>TiO<sub>2</sub> in Situ Formed on the Enhanced Dehydrogenation Properties of NaMgH<sub>3</sub>

Dehydriding Properties of Ti Or/and Zr-doped Sodium Aluminum Hydride Prepared by Ball-Milling

Significantly Improved Dehydrogenation of LiAlH4 Catalysed with TiO2 Nanopowder

Remarkably Improved Hydrogen Storage Properties of Nanocrystalline TiO2-modified NaAlH4 and Evolution of Ti-containing Species During Dehydrogenation/hydrogenation

Investigation on Synthesis, Structure and Catalytic Modification of Ca(AlH4)2 Complex Hydride

Effects of Ti-based Additives on Mg2FeH6 Dehydrogenation Properties

Influence of TiC Catalyst on Absorption/desorption Behaviors and Microstructures of Sodium Aluminum Hydride

TiF4-doped Mg(AlH4)2 with significantly improved dehydrogenation properties

Catalytic effect of Ti on dehydrogenation of Na3AlH6: A first principles investigation

Reversible Hydrogen Storage Properties and Favorable Co-Doping Mechanism of the Metallic Ti and Zr Co-Doped Sodium Aluminum Hydride

Formation of Na3AlH6 from a NaH/Al Mixture and Ti-containing Catalyst

Nature and Role of Ti Species in the Hydrogenation of a NaH/Al Mixture

Influence of Temperature and Hydrogen Pressure on the Hydriding/dehydriding Behavior of Ti-doped Sodium Aluminum Hydride

Catalytic effect of Al3Ti on the reversible dehydrogenation of NaAlH4

Method for Preparing Ti-doped NaAlH4 Using Ti Powder: Observation of an Unusual Reversible Dehydrogenation Behavior