Mechanical Size Effect of Eutectic High Entropy Alloy: Effect of Lamellar Orientation
Yujie Chen,Xianghai An,Sam Zhang,Feng Fang,Wenyi Huo,Paul Munroe,Zonghan Xie
DOI: https://doi.org/10.1016/j.jmst.2020.11.067
2021-01-01
Journal of Material Science and Technology
Abstract:The effect of lamellar orientation on the deformation behavior of eutectic high entropy alloy at the micrometer scale, and the roles of two rarely explored laminate orientations (i.e., the lamellar orientation at similar to 0 degrees and 45 degrees angles with the loading direction) in regulating size-dependent plasticity were investigated using in-situ micropillar compression tests. The alloy, CoCrFeNiTa0.395, consists of alternating layers of Laves and FCC phases. It was found that the yield stress of the 0 degrees pillars scaled inversely with the pillar diameters, in which the underlying deformation mode was observed to transform from pillar kinking or buckling to shear banding as the diameter decreased. In the case of the 45 degrees pillars with diameters ranging from 0.4 to 3 mu m, there exists a 'weakest' diameter of similar to 1 mu m, at which both constraint effect and dislocation starvation are ineffective. Irrespective of the lamellar orientations, the strain hardening rate decreased with decreasing pillar diameter due to the diminishing dislocation accumulation that originated from the softening nature of large shear bands in the 0 degrees pillars, and the enhanced probability of dislocation annihilation at the increased free surfaces in the 45 degrees pillars. The findings expand and deepen the understanding of the mechanical size effect in small-scale crystalline materials and, in so doing, provide a critical dimension for the development of high-performing materials used for nanoor microelectromechanical systems. (C) 2021 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.