Cryo-Scanning Electron Microscopy of Film Formation in Regular and Low-Volatile Organic Contents Waterborne Latex Coatings

Haiyan Ge,Cheng-Le Zhao,Shane Porzio,Li Zhuo,H. T. Davis,L. E. Scriven

DOI: https://doi.org/10.1021/bk-2006-0941.ch006

2006-01-01

Abstract:The film formation processes in regular and low-VOC waterbome latex coatings were compared by cryogenic scanning electron microscopy (Cryo-SEM). Five model MMA/BA/AA/AM copolymer dispersions with particle diameters around 130 nm were used. They were coated on 5mm by 7mm silicon wafers and after 1, 10, and 60 minutes of drying were rapidly frozen in liquid ethane, fractured, sublimated to develop contrast, coated to avoid charging, and examined on the cold stage. Images of the fracture surfaces show top-down and edge-in gradients of consolidation, compaction and coalescence. Some of the low-VOC coatings form a film as fast as conventional ones-or even faster. The findings are corroberated by results of SEM and scanning probe microscopy (SPM) of fracture surfaces and top surfaces of coatings dried for 10 days. Cryo-SEM was also used to compare the degree of swelling and particle shape recovery when the dried coatings were re-hydrated.