Structure and Magnetic Properties of N-doped L10-ordered FePt–C Nanocomposite Films

W. B. Mi,E. Y. Jiang,H. L. Bai,Hui Liu

DOI: https://doi.org/10.1063/1.2170584

IF: 2.877

2006-01-01

Journal of Applied Physics

Abstract:As-deposited and annealed N additive FePt–C nanocomposite films fabricated using facing-target sputtering were investigated systemically. Structure analyses reveal that the as-deposited films are composed of ∼3nm amorphous metal granules buried in a-CN matrix, and transform into L10-ordered FePt particles followed by an increase of particle size after being annealed. The N atomic fraction increases, and the size of FePt particles in the 650°C annealed films reduces, with increasing N2 partial pressure (PN). The diffusion of Fe and Pt atoms into the positions of the ordered L10 lattice was improved by the decompounding of Fe–N bonds and the escape of N atoms from the film during the annealing. Magnetic measurements indicate that high-temperature annealing turns the superparamagnetism (at PN<10%) and paramagnetism (at PN⩾10%) of the as-deposited films into ferromagnetism. The coercivity of the 650°C annealed N-doped films decreases with increasing PN due to the particle size reduction.