Crystal structure of calcite-type Ca1–xMnxCO3 solid solution by X-ray diffraction and Raman spectroscopy
Shanrong Zhang,Wen Liang,Mengzeng Wu,Qifa Zhong,Dawei Fan
DOI: https://doi.org/10.1007/s00269-024-01269-6
IF: 1.748
2024-03-17
Physics and Chemistry of Minerals
Abstract:To investigate the quantitative relationship between the crystal structure and composition of Mn-bearing calcite, the solid solutions of Ca 1– x Mn x CO 3 ( x = 0.1, 0.3, 0.5, 0.7, 0.9) with continuous MnCO 3 mol% content were synthesized at 1 GPa and 700 °C using high-purity CaCO 3 and MnCO 3 powders as starting materials. The run products were analysized by electron probe, powder X-ray diffraction and Raman spectroscopy. The CaO wt% and MnO wt% of the resulting products are consistent with the expected compositions. The powder X-ray diffraction results show that the products are single phase without any impurities. All diffraction peaks of samples with varying MnCO 3 mol% contents can be indexed by the calcite-type structure carbonates ACO 3 ( R-3c space group; A is a divalent cation), confirming the previous results that there is the completely continuous solid solution between CaCO 3 and MnCO 3 end members. The unit-cell parameters and volumes of the solid solutions decrease as the MnCO 3 mol% content increases, presenting a linear relationship of Ca–Mn ideal miscibility, which is perfectly consistent with the rigid body model of A-site substitution in ACO 3 . Besides, as MnCO 3 mol% content increases, the bond distance of A–O decreases linearly, while the bond distance of C–O changes like a parabola. Therefore, the addition of Mn makes the bond distance of A–O shorten, resulting in the decrease of unit-cell parameters and volumes for Ca 1– x Mn x CO 3 . Furthermore, two exterior vibrations (T and L) of the crystal lattice and two internal vibrations (ν 4 and ν 1 ) within the CO 3 2− unit are assigned in the Raman spectra of these solid solutions. The characteristic vibration modes T, L, and ν 4 as a whole increase with the increasing of MnCO 3 mol% content, whereas the characteristic vibration mode ν 1 as a whole decreases with the increase of MnCO 3 mol% content. These variations in Raman vibration modes are related to the radius of substituted ions.
mineralogy,materials science, multidisciplinary