Abstract:ZnO hexagonal sub-microrods have been synthesized onto glass substrates through aqueous growth method by using the thermal decomposition of an aqueous solution of equimolar zinc nitrate(Zn(NO_3)_2·4H_2O) or zinc acetate(Zn(CH_3COO)_2·2H_2O))with methenamine ((CH_2)_6N_4) by controlling the experimental conditions. XRD patterns, SEM images have been measured, which reveals the shape of the most of the ZnO sub-microrods are hexagonal-rod with two flat faces on the two ends, but some are pair rods symmetrically grown from a center to both sides and some form radial clusters from one center. The length of the rods is from 5 μm to 8 μm, the diameter from 300 nm to 700 nm and the ratio of the length to the diameter is more than 10∶1. When the growth time reaches 48 h, we found that the microrods turned into hollow microtubes with the tube-thickness in the tenth of diameter. The growth mechanism is discussed by using the growth model of cathodion ligand tetrahedron. Zn-(NO_3)_2 dissolves and forms growth units of tetrahedron Zn-(OH)_4 under the reaction of the surface activator (CH_2)_6N_4. Then the incorporation of growth units leads to the formation of the ZnO crystal lattice at the interface through a dehydration reaction (OH~-+ OH~-H_2O+O~ 2- ). The fastest of the growth speed along 0001- direction leads to the formation of the ZnO microrods. The reason of forming hollow microtubes is the face of (0001) and 0001- of ZnO rods as eroded by chemical dissolution because of its metastable state. The excitation spectra of ZnO sub-microrods show that except the intrinsic inter-band excitation shorter than 370 nm, there is a strong exciton excitation peak located at around 377~385 nm at room temperature. The photoluminescent spectra show that there is a wide orange-red emission peaking at about 630 nm and FWHM 250 nm with the excitation wavelength 310 nm. When the excitation is a strong 325 nm He-Cd laser, the same sample will emit a strong excition emission peaking at about 385 nm, with FWHM 16 nm and a green emission peaking at about 552 nm with FWHM 120 nm. Compared with the calculated data of these intrinsic defects with the theory of FP-LMTO, the green, orange-red and red emission peaks can be attributed to the transition of oxygen vacancies to the valence band. The studies on PL of ZnO sub-microrods after annealing showed that the excitation peak at about 384 nm disappeared, and the orange-red defect emission (peak at ~630 nm) shows red shift (peak at ~710 nm), and the emission intensity increases. The excitation spectra of samples after annealing showed an enhanced exciton peak at ~377 nm. It indicates that after annealing, the energy transfer from the excition to the defect center occurred.

Photoluminescence Study of ZnO Nanorods Epitaxially Grown on Sapphire (112̄0) Substrates

Dominant Free Exciton Emission in ZnO Nanorods

The Study on Mechanism of Ultraviolet Laser Emission at Room Temperature from Nanocrystal Thin ZnO Films Grown on Sapphire Substrate by L-MBE

Investigation of Luminescence Properties of ZnO Nanowires at Room Temperature

Temperature-dependent Photoluminescence of ZnO Nanorods Prepared by a Simple Solution Route

Photoluminescence Characterization of Nanocrystalline ZnO Array

Photoluminescence and Lasing Properties of Catalyst-Free ZnO Nanorod Arrays Fabricated by Pulsed Laser Deposition

Crystal Growth and Luminescent Properties of ZnO Nanowires Prepared by Thermal Vapor Condensation

Photoluminescence and Low-Threshold Lasing of ZnO Nanorod Arrays.

Photoluminescence and Field Emission of 1D ZnO Nanorods Fabricated by Thermal Evaporation

Crystal Growth and Luminescent Properties of ZnO Sub-microrods Prepared by One Step Solution Growth Method

Temperature and excitation power dependence of photoluminescence of ZnO nanorods synthesized by pattern assisted hydrothermal method

Photoluminescence Properties of Quasialigned Zncdo Nanorods

Crystal Growth and Luminescent Properties of ZnO Sub-microrods and Microrods

Photoluminescence of ZnO Nanowires: A Review

Photoluminescence of Ga-doped ZnO Nanorods Prepared by Chemical Vapor Deposition

Photoluminescence and Raman Spectra in Ga-doped ZnO Layers on Sapphire

Photoluminescence Properties of Zno Nanoneedles Grown by Metal Organic Chemical Vapor Deposition

Rational Synthesis and Tunable Optical Properties of Quasialigned Zn1−xMgxO Nanorods

Horizontal Growth and Ultraviolet Sensitivity Characteristics of ZnO Nanowires on Sapphire Substrates

Synthesis, optical and field electron emission properties of low-dimensional ZnO nano-structures