Melt Electrowriting of Elastic Scaffolds Using PEOT‐PBT Multi‐block Copolymer
Armin Amirsadeghi,Pavan Kumar Reddy Gudeti,Sietse Tock,Marcus Koch,Daniele Parisi,Marleen Kamperman,Małgorzata Katarzyna Włodarczyk‐Biegun
DOI: https://doi.org/10.1002/adhm.202402914
IF: 10
2024-12-12
Advanced Healthcare Materials
Abstract:This study expands the material choices for melt electrowriting by exploring the printability of PEOT‐PBT, a thermoplastic elastomer. Various physicochemical characterizations are performed to study the material's properties before and after printing. Through optimized printing parameters, stable, soft tissue‐compatible scaffolds are produced. The resulting PEOT‐PBT scaffolds support fibroblast viability and reduce α‐SMA expression, offering the potential for tissue engineering applications. Melt electrowriting (MEW) is a powerful additive manufacturing technique to produce tissue engineering scaffolds. Despite its strength, it is limited by a small number of processable polymers. Therefore, to broaden the library of materials for MEW, we investigated the printability of poly(ethylene oxide terephthalate)‐poly(butylene terephthalate) (PEOT‐PBT), a thermoplastic elastomer. The effect of different printing parameters and material thermal degradation are studied. It is observed that the material is stable for >60 min at a printing temperature of 195 °C in a nitrogen environment. Next, two types of designs are printed and characterized: mesh‐like and semi‐random scaffolds. For both types of designs, PEOT‐PBT scaffolds reveal a higher yield strain, and lower Young's modulus as compared to control polycaprolactone scaffolds. Biological studies performed using mouse embryonic fibroblasts (NIH‐3T3) show good cell viability and metabolic activity on all print scaffolds. SEM imaging reveals actively migrating cells on PEOT‐PBT mesh scaffolds after 24 h of culture and 98.87% of pore bridging by cells after 28 days of culture. Immunofluorescence staining shows decreased expression of alpha‐smooth muscle actin from day 14 to day 28 in PEOT‐PBT mesh scaffolds. Overall, it is shown that melt electrowritten PEOT‐PBT scaffolds have great potential for soft tissue regeneration.
nanoscience & nanotechnology,engineering, biomedical,materials science, biomaterials