Transparent Materials with Low Underwater Bubble Adhesion Via Bio-inspired Co-deposition
Yun-peng An,Xin-ning Zhang,Hao-cheng Yang,Xi Yang,Zhi-kang Xu
DOI: https://doi.org/10.11777/j.issn1000-3304.2017.16344
2017-01-01
Abstract:To fabricate hydrophilic/underwater superaerophobic coatings on various transparent materials, such as polystyrene (PS), polypropylene (PP), polymethylmethacrylate (PMMA), polyimide (PI) and polyethylene terephthalate (PET), a co-deposition method of polydopamine (PDA) and polyethyleneimine (PEI) is developed in this work. This method enables one to overcome the obstacle of the bubble adhesion phenomenon in the transparent materials used in underwater devices such as swim goggles and submarine windows. By adding PDA and PEI, a hydrophilic cross-linking network is formed on the material surface via Michael addition or Schiff-base reaction. The modified surface demonstrates improved hydrophilicity, and the water contact angle decreases from 80 degrees to 66 degrees while the submerged gas contact angle increases from 100 degrees to 146 degrees, exhibiting extremely low gas adhesion under water. All these materials are immersed into water during a continuous bubbling process, the PDA/PEI modified surfaces show great gas repellent ability in water on which no obvious bubbles are observed. XPS results and ellipsometer tests show that, with extended deposition time, the amount of the PDA/PEI coating and the thickness of the PDA/PEI coating grow. Meanwhile, the absorption of substrates increases slightly in the visible region with a deposition time below 6 h, which meets the requirements in high transparency and light transmittance. At the same time, the stability of the PDA/PEI coating is measured. After 10 days of submerging and shaking under water, the transparent materials maintain their hydrophilicity and underwater superaerophobicity after deposition, and the sheets exhibit extremely low gas adhesion during underwater bubbling process. Such coating can be applied on various transparent polymer materials such as PP, PMMA, PI and PET (all the submerged gas contact angles are above 140 degrees), which are promising to be used in many submerged devices such as swim goggles, submarine windows, underwater optical lens and transparent shields.