Abstract:Here, the effect of temperature on the electrochemical corrosion of 316L stainless steel (SS) in methyl diethanolamine (MDEA) solution with/without 1.0 wt.% NaCl in the presence/absence of CO2 was investigated using potentiostatic polarization, potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS). The electrochemical measurements showed that although the MDEA solution was highly basic, both chloride and temperature played greater roles in the pitting corrosion of 316L SS, similar to plain NaCl solution. The critical pitting temperature (CPT) of 316L SS in MDEA solution with 1.0 wt.% NaCl decreased from 67.2 oC to 59.6 oC, and the breakdown potential underwent a negative shift of approximately 400 mV, and the EIS Bode impedance decreased. Furthermore, the breakdown potential shifted negatively with increasing temperature when the temperature was lower than CPT in the MDEA solution containing Cl−; however, the breakdown potential decreased slowly, and its temperature dependence was unclear when the temperature was higher than the CPT. In addition, the passive film resistance of 316L SS in all MDEA solutions decreased as the temperature increased. Particularly for the MDEA solution containing Cl−, the passive film resistance decreased by one order of magnitude when the temperature increased from 50 °C to 60 °C. Although the presence of CO2 in the MDEA solution decreased the passive film resistance, it seemed to reduce the individual corrosion contribution of Cl−. The pitting corrosion process of 316L SS in MDEA solution containing chloride ions was discussed by combining these results with classical pitting mechanisms of stainless steel.

The Effects of Chloride Ion Concentration on the Pitting Behavior of 309L Cladding by Using Micro-Electrochemical Measurement and in Situ Optical Observation

Developing a Novel Expression for Chloride Ion Concentration Threshold in Reinforced Concrete: Integration of Electrochemical Analysis and Time-Dependent Modeling

Pitting Corrosion of 304 L Stainless Steel Welds in Simulated Concrete Pore Solutions

The Critical Pitting Chloride Concentration of Various Stainless Steels Measured by an Electrochemical Method

Dependence of Critical Pitting Temperature on the Concentration of Sulphate Ion in Chloride-Containing Solutions

Effect of Chloride Ion Content on Pitting Corrosion of Dispersion-Strengthened-high-strength Steel

SYNERGETIC EFFECT OF FLUORIDE AND CHLORIDE ON THE CRITICAL PITTING TEMPERATURE OF 316 STAINLESS STEEL

Effect of pH and chloride on the micro-mechanism of pitting corrosion for high strength pipeline steel in aerated NaCl solutions

INFLUENCE OF Cl- ON CRITICAL PITTING TEMPERATURE FOR 304 AND 316 STAINLESS STEELS

Accelerating Effect and Critical Ph Value of Occluded Cell Corrosion Within Pits, Crevices, or Stress Corrosion Cracks

Influence of SO4 2- in aqueous solution containing Cl- on the critical pitting corrosion temperature of 316 stainless steel

Influence of SO42- in aqueous solution containing Cl- on the critical pitting corrosion temperature of 316 stainless steel

Effect of Cl- on the Properties of the Passive Films Formed on 316l Stainless Steel in Acidic Solution

Corrosion behaviour of stainless steel exposed to highly concentrated chloride solutions

Effect of temperature on the electrochemical pitting corrosion behavior of 316L stainless steel in chloride-containing MDEA solution

Impact of NaCl impurity on corrosion of 316 L steel in molten nitrate salts for thermal energy storage: An electrochemical study

Direct observation of pitting corrosion evolutions on carbon steel surfaces at the nano-to-micro- scales

Metastable pitting corrosion behavior and characteristics of passive film of laser powder bed fusion produced Ti–6Al–4V in NaCl solutions with different concentrations

Chloride-induced alterations of the passive film on 316L stainless steel and blocking effect of pre-passivation

Failure analysis of anion synergy on pitting behavior of liner 316L in sour water system by electrochemical tests

Systematic Insight into Chloride Concentration, Applied Potential and Time Effect on the Passive Film of Cu-Zn-Ni Ternary Alloy in Alkaline Solution