Abstract:Stiffness degradation due to matrix cracks is the main initial form of damage in composite laminates. This paper presents a framework to model geometrically nonlinear large deformation behaviors of matrix cracked hybrid composite double-curved deep shell containing carbon nanotube reinforced composite (CNTRC) layers. Two types of structures, namely Structure-I and Structure-II, are investigated. The CNTRC layers in Structure-I are considered with CNTs arranged in uniformly distributions, while Structure-II is arranged in functionally graded distributions. The degraded stiffness of cracked layers is modeled via the self-consistent model (SCM) micromechanical framework. To describe the geometrically nonlinear large deflection behaviors and account for deep and moderate thick shells, the von Kármán geometric nonlinearity assumptions and the term 1/(1+ς/R) are considered in the relationship between displacement and strain. The IMLS-Ritz method is employed to discretize the non-linear partial differential equations. The modified Newton–Raphson method in combination with the arc-length iteration technique is adopted to solve the discretized equations. Comparison studies indicate that the proposed predictive model can furnish very accurate results for linear and nonlinear behaviors of thin to moderately thick as well as shallow and deep laminated doubly-curved shells. Parametric studies on the effect of CNT distribution, matrix crack density, load type, length-to-thickness ratio, radius-to-length ratio, aspect ratio, boundary condition, and fiber ply-angle on the geometrically nonlinear large deformation behaviors of spherical hybrid composite shells are investigated.

Progressive Damage Analysis for Multiscale Model of Linerless Composite Cryotank and Integrated Design

Mechanical Analysis and Optimal Design for Carbon Fiber Resin Composite Wound Hydrogen Storage Vessel With Aluminum Alloy Liner

Continuum Damage Modeling and Progressive Failure Analysis of Carbon Fiber/epoxy Composite Pressure Vessel

Mechanical Analysis of Carbon Fiber Filament Wound Hydrogen Storage Vessel with Aluminum Alloy Liner

Progressive failure analysis of 2D woven composites at the meso-micro scale

Micromechanics-based Progressive Failure Analysis of Carbon FIber/epoxy Composite Vessel under Combined Internal Pressure and Thermomechanical Loading

Mechanical Analysis and Reasonable Design for Ti-Al Alloy Liner Wound with Carbon Fiber Resin Composite High Pressure Vessel

Micromechanics-based Burst Failure Analysis of Composite Vessel Used for Hydrogen Storage

A low-cost multiscale model with fiber/matrix interface for cryogenic composite storage tanks considering temperature effects based on self-consistent clustering analysis

Mechanical Analysis and Optimal Control of Hydrogen Storage Vessels with Carbon Fiber Filament Wound Aluminum Liner

Multi-Scale Failure Analysis Model for Cryogenic Pressure Vessel Under Combined Thermal Stress and Mechanical Stress

An Integrated Approach to Analyzing Matrix-Crack-induced Stiffness Degradation and Medium Leakage in Linerless Composite Vessels

Progressive Failure Analysis and Burst Mode Study of Type IV Composite Vessels

Instability Analysis and Development of High Pressure Hydrogen Storage Vessels

Progressive damage analysis for multiscale modelling of composite pressure vessels based on Puck failure criterion

Multiscale Progressive Failure Analysis for Composite Stringers Subjected to Compressive Load

Finite Element Analysis of Burst Pressure of Composite Hydrogen Storage Vessels

Stress and Damage Analyses of Composite Overwrapped Pressure Vessel

Modeling Geometrically Nonlinear Large Deformation Behaviors of Matrix Cracked Hybrid Composite Deep Shells Containing CNTRC Layers

Progressive damage analysis of double-layer variable thickness 3D woven composite scaled engine casing

A unified modeling strategy of the stability and progressive damage behavior of CFRP double-blade composite stiffened structures (DCSS) under uniaxial compression