Influences of Initial Microstructures on Martensitic Transformation and Textures During Cold Rolling and Tensile Mechanical Properties in High Manganese TRIP Steel

Dan-dan Ma,Ping Yang,Xin-fu Gu,Feng-E Cui

DOI: https://doi.org/10.1016/j.msea.2021.142147

IF: 6.044

2021-01-01

Materials Science and Engineering A

Abstract:The deformation-induced transformation characteristics and texture evolution of α′-martensite during cold rolling together with the tensile properties of two specially prepared initial microstructures (bimodal elongated γ grains and fine equiaxed γ grains) were investigated in high manganese TRIP steels. The results showed that the thermally induced martensite was restrained effectively by refining grains or introducing crystal defects like dislocations, which provided a nearly full austenite phase for the subsequent TRIP process. Compared with the solution-treated sample containing coarse equiaxed γ grains, the fine-grained sample revealed a better plasticity and a higher strength due to grain refinement and progressive TRIP process. The bimodal elongated-grained sample exhibited the highest strength and sufficient plasticity because the dislocation strengthening exceeded the fine-grain strengthening and martensitic transformation was delayed. The transformation textures of two kinds of samples differed in that the fine-grained sample demonstrated typical {113}<110>α from the Copper-type γ texture and {332}<113>α from the Brass-type γ texture, whereas {001}<110>α texture occurred in the bimodal elongated-grained sample in addition to the above two components. In the early stage of TRIP, there was an obvious orientation dependence, and the {100}- and Copper-oriented γ grains preferentially transformed to martensite rather than γ grains with Brass orientation.