Comparative Study on the Properties of Wood Vinegar Prepared from the Pretreated Chinese Fir: Effect of Hydrothermal Parameters and Hydrogen Peroxide
Jiaqing Xu,Shouyu Zhang,Yi Zhou,Simeng Liu,Sen Lang,Jifan Yang,Yuxin Wu
DOI: https://doi.org/10.1016/j.jaap.2022.105674
IF: 6
2022-01-01
Journal of Analytical and Applied Pyrolysis
Abstract:Hydrothermal (HT) pretreatment and hydrothermal oxidative (HO) pretreatment are efficient in upgrading the quality of wood vinegar (WV), while little research pays attention to the systemic comparison between the effects of HT and HO pretreatment on the resulted WV. Therefore, in the present study, the response surface method is adopted first to analyze the effect of HT temperature, solid-to-liquid ratio (S/L), and retention time on the physicochemical properties of WV prepared from Chinese fir (CF). Then, the main compositions (hemicellulose, cellulose, and lignin) of the pretreated CF are quantitatively measured, and the comparative study between the effects of HT pretreatment and HO pretreatment on the yield, density, and compositions of the resulted WV is carried out based on CF composition. The results show that HT temperature is the main parameter that affects the physicochemical properties of the resulted WV. With the increase of HT temperature, the cellulose content of CF samples increases first at 180-230 degrees C and then decreases at 260-280 degrees C, the hemicellulose content decreases, and the lignin enriches. The cellulose enrichment gives rise to the increasing WV yield at 180-200 degrees C and the increasing WV density at 180-230 degrees C. While the dramatic cellulose decomposition at 230-280 degrees C results in the decreasing WV yield at 230-280 degrees C and the decreasing WV density at 260-280 degrees C. The cellulose is the main component that contributes to the yield and density of WV. Moreover, due to the cellulose enrichment, the contents of the organic compounds, especially the phenols, ketones, and aldehydes, increase dramatically at 180-230 degrees C, contributing to the lower pH value of the resulted WV. However, HO pretreatment aggravates the decomposition of CF components. During HO pretreatment, the decreases in the hemicellulose content and cellulose content are advanced to 160-200 degrees C and 180-230 degrees C respectively, and the lignin content increases. Thus, WV with the comparable yield and density to the unpretreated WV can be prepared at HO pretreatment temperature of 160 degrees C. Moreover, the pH value of WV decreases significantly after HO pretreatment of 160-200 degrees C because of the existence of the acid compounds with higher acidity in the resulted WV. Meanwhile, the content of the aldehydes contained in WV prepared from HO pretreated CS increases dramatically.