In-situ Phosphating Co@Nitrogen-doping Graphene Boosts Overall Water Splitting under Alkaline Condition

Dongfeng Sun,Songmin Lin,Yuan Yu,Fangyou Meng,Gaohui Du,Bingshe Xu
DOI: https://doi.org/10.1016/j.jelechem.2021.115882
2021-01-01
SSRN Electronic Journal
Abstract:Design and synthesis highly-efficiency and noble-metal-free electrocatalysts for hydrogen/oxygen evolution reaction (HER/OER) is still critical and challenged. Herein, we develop an in-situ phosphating Co@nitrogen-doping graphene to obtain N and P co-doped carbon-coated cobalt phosphide (CoP@N,P-C) for overall water splitting. The presence of unique 3D porous sponge structure in CoP@N,P-C offers abundant catalytic active sites and accelerated penetration of electrolyte solution that facilitates the transfer of ions. Subsequently, the synergy between the CoP cores and N, P-C shells improves the total hydrolysis performance of electrocatalyst in HER and OER processes. At the current densities of 10 mA/cm2 in 1 M KOH, the HER overpotential of the CoP@N,P-C is 113 mV, and its OER overpotential is 320 mV. Moreover, the cell voltage of the CoP@N,P-C as bifunctional electrode for overall water splitting was 1.67 V (at 10 mA/cm2), which is close to that of the full noble-metal electrode (RuO2|| Pt/C, 1.58 V). Overall, CoP@N, P-C bifunctional catalyst shows great potential for replacing noble-metal electrodes in water splitting application.
What problem does this paper attempt to address?