Abstract:Fretting fatigue pertains to the behaviour of engineering components undergoing cyclic loading while in contact with each other. This intricate contact-related phenomenon often results in premature failure compared to conventional fatigue issues. Moreover, when these components operate in high-temperature atmospheres and experience high wear conditions, such as the heat transfer tubes in the nuclear reactor, the application of Functionally Graded Material (FGM) coatings becomes essential. Consequently, it is imperative to investigate how FGM coatings influence the initiation and propagation behaviour of fretting fatigue cracks. This paper employs the Critical Plane (CP) Method to calculate the damage parameter. Additionally, Linear Elastic Fracture Mechanics (LEFM) criteria, specifically the Extended Maximum Tangential Stress (E-MTS) criterion, are utilized to examine how FGM coatings affect the paths of crack propagation in the presence of fretting conditions. Meanwhile, due to the unavailability of material properties for FGM coatings, the damage parameter and stress intensity factors are utilized to indirectly assess the effect of FGM coatings on crack initiation and propagation lifetime. The FGM coating significantly influences tangential stress, thereby affecting the length of the stick zone, while having minimal impact on the distribution of normal stress along the contact surface. Furthermore, it is observed that adjusting the descent ratio of FGM coatings and the elastic modulus of the first FGM coating layer provides a potential avenue for enhancing both crack initiation and propagation lifetimes.

Fretting Fatigue Crack Monitoring in Aero-Engine Turbine Tenon Connection Structure Using Silicon Based Replica Method

Fatigue Crack Propagation Analysis in an Aero-Engine Turbine Disc Using Computational Methods and Spin Test

Depth-sensing Indentation Measurement and Finite Element Analysis of Residual Stress Field Near Fatigue Crack Tip

A Hybrid Modeling Method of Fatigue Crack Growth for Gas Turbine Blades under Combined High and Low Cycle Fatigue Loadings

An investigation of high and room temperature fretting fatigue of DD6-FGH96 dovetail joint in aero-engine: Experimental and numerical analysis

Numerical Study on Fretting Wear of DZ125/FGH99 Tenon/Mortise Joint Structure

Very High Cycle Fretting Fatigue Damage and Crack Path Investigation of Nimonic 80A at Elevated Temperature

In-situ SEM and EBSD Study on Fretting Fatigue Crack Initiation of a Directionally Solidified Ni-based Superalloy

Ti-6Al-4V fretting wear and a quantitative indicator for fretting regime evaluation

Experimental and Analytical Investigation for Fatigue Crack Growth Characteristics of an Aero-Engine Fan Disc

Thermomechanical Fatigue Experiment and Failure Analysis on a Nickel-Based Superalloy Turbine Blade

Experimental study of fretting fatigue in dovetail assembly considering temperature effect based on damage mechanics method

Fretting fatigue damage mechanism of Nickel-based single crystal superalloys at high temperature

Thermomechanical Fatigue Damage Mechanism and Life Assessment of a Single Crystal Ni-based Superalloy

An Arc-tenon Attachment for Nickel-based Single Crystal Turbine Blade with Improved High-Temperature Fretting Fatigue Performance

Fretting fatigue crack initiation and propagation behaviours of Ti6Al4V alloy coated by functionally graded material

A critical-plane-based thermomechanical fatigue lifetime prediction model and its application in nickel-based single-crystal turbine blades

Analysis of Fatigue Cracking for Turbine Blade

Fretting Fatigue Behavior of Riveted Al 6XXX Components

Fretting Fatigue Analysis of Additively Manufactured Blade Root Made of Intermetallic Ti-48Al-2Cr-2Nb Alloy at High Temperature

In-situ Observation and Finite Element Analysis of Fretting Fatigue Crack Propagation Behavior in 1045 Steel