Abstract:Chloride ion erosion is an important factor affecting the durability of marine engineering concrete. In particular, concrete structures in wave splash and tidal zones are subjected to dry and wet cycles and multidimensional diffusion of chloride ions. To investigate the intricate diffusion of chloride ions within concrete under these dynamic conditions, we devised a comprehensive experiment. This experiment encompasses multiple dimensions, involving dry and wet cycles, as well as static immersion. The experiment intends to reveal how chloride ions are distributed in the concrete and clarify the changes that occur in its microstructure. Based on Fick's second law, the multidimensional diffusion model of chloride ions in concrete under the dry and wet cycles and static immersion was established by comprehensively considering the effects of chloride ion exposure time, environment temperature, relative humidity, and the action of dry and wet cycles. The results show that, under the same conditions, the chloride content in concrete decreases with the increase in penetration depth but increases with the increase in the chloride diffusion dimension and exposure time. Dry and wet cycles and multidimensional diffusion of chloride ions increase the development of cracks and pores in the concrete structure and generate large quantities of C3A·CaCl2·10H2O, which will exacerbate the chloride ion transport rate and penetration depth of concrete. Under the same exposure time and penetration depth, the chloride ion content in concrete under two-dimensional (2D) and three-dimensional (3D) diffusion under dry and wet cycles was 1.09~4.08 times higher than that under one-dimensional (1D) diffusion. The correlation coefficients between the simulation results of the multidimensional transport model of chloride ions in concrete under multi-factor coupling and the experimental results were all greater than 0.95, and the model can be utilized to predict the distribution of chloride ion concentration in concrete.

Experiment and Simulation of Chloride Ion Transport and Binding in Concrete under the Coupling of Diffusion and Convection

Theoretical and Experimental Investigation of Loading Effects on Chloride Diffusion in Saturated Concrete

Diffusion Model Of Chloride Ion In Concrete And Its Verification

Comparative Study On Testing Methods Of Chloride Ions Diffusion Coefficient In Concrete

Numerical Simulation of Chloride Penetration in Concrete in Rapid Chloride Migration Tests

Convection-diffusion-electromigration coupled numerical simulation of water and chloride in cement-based materials

EXPERIMENTAL STUDY ON THE CHLORIDE DIFFUSION OF CONCRETE BASED ON ITS PORE STRUCTURE

MECHANISM AND MATHEMATIC MODELING OF CHLORIDE PERMEATION IN CONCRETE UNDER UNSATURATED STATE

Investigation on the Transport Properties of Chlorides in Concrete II Numerical Simulation

A Multi-Phase Model for Predicting the Effective Diffusion Coefficient of Chlorides in Concrete

Experimental Study on Chloride Ion Transport in Concrete Structure under Shear Stress

A Numerical Study on Chloride Migration in Cracked Concrete Using Multi-Component Ionic Transport Models

Chloride Ion Ingress Distribution Within an Alternate Wetting-Drying Marine Environment Area

Numerical and Experimental Study of Moisture and Chloride Transport in Unsaturated Concrete

Chloride Penetrating under Co-Effects of Initial Curing and Exposure Conditions

Experimental and Numerical Study on the Microstructure and Chloride Ion Transport Behavior of Concrete-to-concrete Interface

Multidimensional Transport Experiment and Simulation of Chloride Ions in Concrete Subject to Simulated Dry and Wet Cycles in a Marine Environment

Numerical Simulation of Ionic Transport in Cement Paste under the Action of Externally Applied Electric Field

CHLORIDE ION TRANSPORT IN COVER CONCRETE UNDER DRYING-WETTING CYCLES:THEORY,EXPERIMENT AND MODELING

Modelling of Chloride Penetration in Unsaturated Concrete

A Multiphase Numerical Simulation of Chloride Ions Diffusion in Concrete Using Electron Microprobe Analysis for Characterizing Properties of ITZ